水性环氧在建筑砂浆上应用性能的研究  

Properties of Waterborne Epoxy Mortar in Architectural Applications

作　　者：沈志明[1,2] 李安宁[1,2] 朱殿奎[1,2] 李晴[1,2] 李娟[1,2] 杨亚萍[1,2] 

机构地区：[1]江苏丰彩新型建材有限公司,江苏南京211100 [2]江苏省既有建筑绿色化改造工程技术研究中心,江苏南京211100

出　　处：《江苏建筑》2016年第B12期83-85,共3页Jiangsu Construction

摘　　要：文章对自制水性环氧乳液改性砂浆中一系列影响因素进行研究,结果表明:脱模后水性环氧改性砂浆在自然养护条件下3d中,然后置于养护室(湿度90%)中4d,最后置于自然养护中28d后,水性环氧乳液最佳添加比例为12%时,抗折强度,抗压强度分别为15.9MPa,78.4MPa;拉伸粘结强度达到了5.3MPa.获得最佳力学性能,自制水性环氧改性砂浆试样具有明显的增益效果。In this paper, homemade waterborne epoxy emulsion modified mortar series of factors were studied, the results showed that： after releasing waterborne epoxy-modified mortar in natural curing for 3 days and then placed in curing room （90% humidity） in when four days, finally put nature conservation in 28 days, waterborne epoxy emulsion optimum addition ratio is 12%, flexural strength, compressive strength of 15.9MPa, 78.4MPa; tensile bond strength reaches 5.3MPa. optimum mechanical properties, homemade waterborne epoxy- modified mortar specimens with a significant gain results.

关 键 词：水性环氧乳液 建筑砂浆 水性固化剂 

分 类 号：TU578.1[建筑科学—建筑技术科学]