碳酸钙晶须对碱激发矿渣力学和热稳定性能的影响  

Effect of CaCO_3 Whisker on Mechanical and Thermal Stability Properties of Alkali Activated Slag

作　　者：龙辉[1] 赵英良[1] 邢军[1] 邱景平[1] 孙晓刚[1] 

机构地区：[1]东北大学资源与土木工程学院,沈阳110819

出　　处：《硅酸盐通报》2017年第2期697-700,711,共5页Bulletin of the Chinese Ceramic Society

基　　金："十二五"国家科技支撑计划(2012BAJ17B01;2012BAJ17B02)

摘　　要：为探讨CaCO_3晶须对碱激发矿渣的强化机理,本文研究了不同晶须掺量(0%~9%)对碱激发矿渣力学和热稳定性能的影响,研究结果表明:CaCO_3晶须可通过减少基体的微裂隙从而显著提高碱激发材料的力学性能;当晶须用量为6%时,强化效果达到最佳,碱激发材料的抗压和抗弯强度分别提高了22.7%和79.9%,另外由于CaCO_3晶须在低于650℃时具有较高的热稳定性,因此,在此温度区间内掺加晶须的碱激发材料的热稳定性得到了显著强化。In order to explore the reinforcement of CaCO_3 whisker in alkali activated slag,the effect of CaCO_3 whisker content（ 0%-9%） on the mechanical and thermal properties of alkali activated slag were studied. The results showed that CaCO_3 whisker could improve the mechanical properties of alkali activated slag through reducing the micro cracks in the matrix. The compressive and flexural strength of alkali activated slag reinforced by 6% of CaCO_3 whisker were increased by 22. 7% and 79. 9%,respectively. On the other hand,the thermal stability of CaCO_3 whisker reinforced alkali activated slag was enhanced before 650 ℃ due to the stability of CaCO_3 whisker.

关 键 词：碱激发矿渣 碳酸钙晶须 力学性能 热稳定 微观结构 

分 类 号：X703[环境科学与工程—环境工程]