Al-MCM-41介孔分子筛成型工艺  

The Forming Process of Al-MCM-41

作　　者：何锡凤[1] 宋伟明[1] 张挥球[1] 徐昊妍[1] 

机构地区：[1]齐齐哈尔大学化工与化学工程学院,黑龙江齐齐哈尔161006

出　　处：《化工时刊》2017年第1期1-4,共4页Chemical Industry Times

基　　金：黑龙江省教育厅面上项目(12511595)

摘　　要：本文研究了Al-MCM-41的成型工艺。通过氮气吸附-脱附,程序升温脱附(NH_3-TPD)等表征方法,对在不同条件下成型的Al-MCM-41分子筛(CX-Al-MCM-41)进行分析,考察了成型条件对催化剂酸量、孔道结构、侧压强度等的影响。实验结果表明当γ-Al_2O_3用量为30%,聚乙二醇用量为5%,丁烷四羧酸用量为3%,v(10%HNO3)∶m(Al-MCM-41))=1.0∶1.5时,成型后催化剂的宏观物性最佳,其最大侧压强度可达48 N·cm^(-1)。Abstract The forming process and catalytic properties of Al - MCM -41 were studied. Effects of molding conditions of forming CX- Al- MCM-41 on the catalyst acidity, pore structure and the edgewise compressive strength were investigated by nitrogen adsorption desorption, temperature programmed desorption （ NH3 - TPD） and other characterization methods. The results showed that the edgewise compressive strength of CX -Al -MCM -41 was up to 48 N · cm1 when the AlzO3 content was 30%, the polyethylene glycol （PEG） was 5%, the polycarboxylic acid dosage was 3% and v （10% HNO3）： m（Al-MCM-41）） was 1.0： 1.5.

关 键 词：AL-MCM-41 催化剂成型 侧压强度 

分 类 号：TQ424.25[化学工程]