波导制备用铒镱掺杂磷酸盐玻璃的光学光谱参数  

Optical and spectral parameters of Er^(3+) and Yb^(3+) co-doped phosphate glass for waveguide fabrication

作　　者：申权[1] 张晶晶[2] 柳鸣[2] 王志强[2] 赵昕[1] 

机构地区：[1]大连工业大学信息科学与工程学院,辽宁大连116034 [2]大连工业大学纺织与材料工程学院,辽宁大连116034

出　　处：《大连工业大学学报》2017年第1期54-57,共4页Journal of Dalian Polytechnic University

基　　金：辽宁省教育厅科学技术研究项目(L2014226)

摘　　要：制备了一种具有优异化学稳定性的碱性铝磷酸盐玻璃,将该玻璃样品浸入390℃下的KNO_3熔盐中离子交换2h后得到了平面波导。有效扩散系数为0.11μm^2/min,说明该玻璃实现了高效的离子交换。通过光谱分析可得,~4I_(13/2)→~4I_(15/2)能级跃迁的半高宽和最大发射截面分别为30nm和6.80×10^(-21)cm^2。结果表明,当~4I_(13/2)能级上Er^(3+)的比例达到80%时,计算得到的理论增益可以达到2.97dB/cm。Alkaline aluminum phosphate glasses were fabricated, and planar waveguide was obtained on Er^3＋/Yb^3＋ co-doped NMAP glass after submerging the glass sample into the KNO3 fused salt under 390 ℃ for 2 h. The effective diffusion coefficient was deduced to 0.11 μm2/min, indicating that the ion exchange process was achieved efficiently. According to the spectrum analysis, the full width at half maximum and maximum stimulated emission cross section of ^4I13/2→^4I15/2 energy level transition were 30 nm and 6.80 ×10^-21cm^2. Results showed that the calculated theoretical gain could achieve 2.97 dB/cm when the ratio of Era＋ in 4I13/2 energy level reached to 80%.

关 键 词：铒镱共掺 磷酸盐玻璃 钾钠离子交换 光波导 

分 类 号：TQ160.5[化学工程—高温制品工业]