Static recrystallization behavior of 25CrMo4 mirror plate steel during two-pass hot deformation  

作　　者：Peng Zhou Qing-xian Ma 

机构地区：[1]Department of Mechanical Engineering, Tsinghua University, Beijing 100084, China [2]Key Laboratory for Advanced Materials Processing Technology of Ministry of Education, Tsinghua University, Beijing 100084, China

出　　处：《Journal of Iron and Steel Research International》2017年第2期222-228,共7页

基　　金：sponsored by National Basic Research Program of China (2011CB012903)

摘　　要：The static recrystallization behavior of 25CrMo4 mirror plate steel has been determined by hot compression testing on a Gleeble 1500 thermal mechanical simulation tester. Compression tests were performed using double hit schedules at temperatures of 950-- 1 150 ~C, strain rates of 0.01--0.5 s-1 , and recrystallization time of 1--100 s. Results show that the kinetics of static recrystallization and the microstructural evolution were greatly influenced by the deformation parameters （deformation temperature, strain rate and pre strain） and the initial austenite grain size. Based on the experimental results, the kinetics model of static recrystallization has been generated and the comparison between the experimental results and the predicted results has been carried out. It is shown that the predicted results were in good agreement with the experimental results.The static recrystallization behavior of 25CrMo4 mirror plate steel has been determined by hot compression testing on a Gleeble 1500 thermal mechanical simulation tester. Compression tests were performed using double hit schedules at temperatures of 950-- 1 150 ~C, strain rates of 0.01--0.5 s-1 , and recrystallization time of 1--100 s. Results show that the kinetics of static recrystallization and the microstructural evolution were greatly influenced by the deformation parameters （deformation temperature, strain rate and pre strain） and the initial austenite grain size. Based on the experimental results, the kinetics model of static recrystallization has been generated and the comparison between the experimental results and the predicted results has been carried out. It is shown that the predicted results were in good agreement with the experimental results.

关 键 词：Hot deformation Static recrystallization 25CrMo4 Kinetics equation Microstructure 