AZ91D镁合金化学沉积Ni-P合金镀层工艺研究  

Technology Research on Electroless Plating of Ni-P Alloy Coating on AZ91D Magnesium Alloy

作　　者：陈婷婷[1] 亢淑梅[1] 赵超山 李欣妍[1] 陈华 

机构地区：[1]辽宁科技大学材料与冶金学院,辽宁鞍山114051 [2]鞍钢股份产品发展部,辽宁鞍山114051

出　　处：《电镀与精饰》2017年第4期5-8,共4页Plating & Finishing

基　　金：辽宁科技大学大学生创新创业训练计划项目资助(DC2016005)

摘　　要：为提高镁合金的耐蚀性,以AZ91D镁合金为基体,采用化学沉积方法制备了Ni-P合金镀层。利用维氏硬度仪、扫描电镜、能谱分析仪及Autolab电化学工作站等检测方法,分析了镀层的硬度、显微形貌、镀层成分及耐蚀性。结果表明,HF质量浓度为200 m L/L、活化t为15 min、镀液p H为7.30时能有效提高镀层的耐蚀性。Ni-P alloy coating was prepared on AZ91D magnesium alloy substrate by electroless plating to improve its corrosion resistance. The hardness, microstrueture morphologies, coating composition and corrosion resistance of the coating were studied by Vickers hardness tester, scanning electron microscopy, energy dispersive spectroscopy and electrochemical workstation Autolab. Results showed that when the HF acid concentration was 200 mL/L, activation time was 15 min and the bath pH was 7.30, the coating corrosion resistance could be improved obviously.

关 键 词：化学沉积Ni-P合金 镁合金 活化 p H 耐蚀性 

分 类 号：TQ153.12[化学工程—电化学工业]