单体纯度对α-氰基丙烯酸酯胶性能的影响  

Effect of monomer purity on performance of α-cyanoacrylate adhesive

作　　者：刘洁 LIU Jie(Beijing Tonson Adhesive Co., Ltd., Beijing 100041, China)

机构地区：[1]北京天山新材料技术有限公司,北京100041

出　　处：《粘接》2017年第5期45-47,共3页Adhesion

摘　　要：选用单体α-氰基丙烯酸乙酯、增韧剂、稳定剂及其他助剂制备了2种α-胶样,其中样1的单体纯度较高,样2的单体纯度较低,其余组分相同。通过对比2种胶样的性能发现,单体纯度较高的样1在固化时间、耐热性、耐湿热方面都明显高于单体纯度较低的样2,单体纯度对热老化性能的影响不大。In this work, we prepared two α-cyanoacrylate adhesive samples （1 and 2）, which mainly comprise the ethyl α-cyanoacrylate monomer, toughening agent, stabilizer and other additives. Sample 1 and 2 used the high purity monomer and the low purity monomer, respectively, and other components were same. The results indicated that sample 1 showed improved cure speed, hot strength and wet heat resistance, compared to sample 2, and the effect of monomer purity on the heat ageing property was not obvious.

关 键 词：氰基丙烯酸乙酯 纯度 性能 

分 类 号：TQ433.43[化学工程]