SiO_2/CrO_x/CrN_y/Al太阳能选择性吸收涂层盐雾腐蚀性能分析  

ANALYSIS OF CORISION RESISTANCE PERFORMANCE OF SiO_2/CrO_x/CrN_y/Al SOLAR SELECTIVE ABSORBING COATINGS

作　　者：魏东辉[1] 李文哲[1] 房俊龙[1] 

机构地区：[1]东北农业大学电气与信息学院,哈尔滨150030

出　　处：《太阳能学报》2017年第4期1087-1091,共5页Acta Energiae Solaris Sinica

基　　金：哈尔滨市应用技术研究与开发项目(2013RFQXJ094)

摘　　要：对SiO_2/CrO_x/CrN_y/Al型太阳能光谱选择性吸收涂层的盐雾腐蚀性能进行测试。在35℃下经质量分数为1%、3%、5%的NaCl盐雾处理一系列时间后采用UV、VIS、NIR、FTIR、SEM等方法表征该涂层腐蚀后光学性能及表面形貌的变化。结果表明经不同浓度的NaCl盐雾腐蚀后涂层出现表面粗糙度增加、白色斑点、起泡等缺陷。光学性能的衰减规律为:吸收比呈指数衰减,发射比初期迅速增加,然后进入钝化期,最后进入过钝化期而再次迅速增加。The salt spray corrosion resistance performance of SiO2/CrO=/CrNr/A1 selective absorption coatings for solar spectrum was tested. UV-VIS-NIR, FTIR, SEM were used to characterize the changes in optical properties and surface appearance of the coating after being treated with NaC1 salt spray at a mass fraction of 1%, 3% and 5% at 35℃. The results show that the increase of surface roughness, white spots, blistering and other defects appear in the coating after NaC1 salt spray corrosion. The attenuation of the optical properties performs that the absorption rate exponentially decays, the emitting rate increases rapidly in the initial period, and then steps into the passivation period, and finally steps into the over passivation period and rapidly increases again.

关 键 词：太阳能光谱选择性吸收涂层 CrOx CrNy 盐雾腐蚀 腐蚀规律 

分 类 号：TG144[一般工业技术—材料科学与工程]