颜填料含量对水性环氧树脂防腐蚀涂料性能的影响  

Waterborne epoxy resin anti influence of pigment and filler content on the performance of anticorrosive coating formulation

作　　者：张霞[1] 

机构地区：[1]酒泉职业技术学院,甘肃酒泉735000

出　　处：《中国建材科技》2017年第2期61-62,共2页China Building Materials Science & Technology

基　　金：酒泉职业技术学院院级科研项目<在恶劣环境下钢结构工业建筑中水性环氧树脂防腐涂料的性能研究>(项目编号xyjy[2015]Y-3)

摘　　要：本文根据涂料的防腐蚀机理,探讨以环氧树脂为基料的水性防腐蚀涂料中颜填料含量对涂料性能的影响。本文主要选用磷酸锌作为防锈颜料,根据CPVC/PVC的变化对涂料性能影响的理论,设计配方组成含量。然后通过调整三聚磷酸铝、铁红、硫酸钡颜料用量,观察涂料防腐性能的变化。探讨了三聚磷酸铝、氧化铁红、硫酸钡颜料Fe_2O_3含量对漆膜的性能的影响。In this paper, the effect of pigment and filler content on the properties of waterborne anticorrosive coatings based on epoxy resin was studied in this paper. In this paper, zinc phosphate as anti rust pigment, according to the change of CPVC/PVC on the performance of the coating theory, design formula composition content. Then through adjusting the amount of aluminum phosphate, Tie Hong and barium sulfate, the change of coating anticorrosion property was observed. The effect of the content of aluminum, iron oxide red and barium sulfate on the properties of paint film was discussed.

关 键 词：防腐蚀 三聚磷酸铝含量 氧化铁红含量 硫酸钡颜料Fe2O3含量 涂料性能 

分 类 号：TU503[建筑科学—建筑技术科学]