Deterioration Process of the Hybrid Films during Wear Test--Polyacrylate Emulsion Modified by Silica Particles  

作　　者：YANG Mingjun DENG Binbin YUAN Feifei 

机构地区：[1]School of Materials Science and Engineering, Southwest Petroleum University

出　　处：《Wuhan University Journal of Natural Sciences》2017年第3期191-196,共6页武汉大学学报（自然科学英文版）

基　　金：Supported by the Southwest Petroleum University Outstanding Researcher Grant(201331010015)

摘　　要：The hybrid materials are widely used in various fields for excellent performance. However, there are few researches studying their failure process. In order to prepare the hybrid materials with better performance, the failure process needs to be well studied. Two kinds of silica/polyacrylate films are successfully prepared to study the effect of organic-inorganic interaction on performance. The average diameter of silica particles is measured to be around 342 nm by scanning electron microscope（SEM）. Wear test demonstrates the hybrid film, which is obtained by grafting polyacrylate onto silica particles, possesses more excellent properties than the one filled directly with silica particles. The stronger interaction between organic and inorganic components leads to a better distribution of inorganic particles within the polymer matrix. In this work, a model is presented to illustrate the deterioration process of the hybrid films, which allows us to further understand the hybrid materials.The hybrid materials are widely used in various fields for excellent performance. However, there are few researches studying their failure process. In order to prepare the hybrid materials with better performance, the failure process needs to be well studied. Two kinds of silica/polyacrylate films are successfully prepared to study the effect of organic-inorganic interaction on performance. The average diameter of silica particles is measured to be around 342 nm by scanning electron microscope（SEM）. Wear test demonstrates the hybrid film, which is obtained by grafting polyacrylate onto silica particles, possesses more excellent properties than the one filled directly with silica particles. The stronger interaction between organic and inorganic components leads to a better distribution of inorganic particles within the polymer matrix. In this work, a model is presented to illustrate the deterioration process of the hybrid films, which allows us to further understand the hybrid materials.

关 键 词：hybrid materials deterioration mechanism silica/polyacrylate films 