超声机械镀铜的性能研究  

Study on the Performance of Ultrasonic Mechanical Cu Plating

作　　者：夏汝岩 牛宗伟[1] 王宏甲[1] 张兴武[1] 丁兆勇[1] 

机构地区：[1]山东理工大学机械工程学院,山东淄博255000

出　　处：《电镀与精饰》2017年第5期1-4,共4页Plating & Finishing

基　　金：国家自然科学基金(51005140);山东省自然科学基金(2015ZRB01917);山东理工大学青年教师发展支持计划经费资助

摘　　要：利用超声机械镀实验装置制备了性能良好的铜镀层,借助扫描电子显微镜及能谱仪,分析铜镀层的外观、结合强度、表面形貌及化学组成,并对镀铜层抗腐蚀性能进行测试。结果表明,超声机械铜镀层色泽均匀且致密,与基体结合强度良好,耐腐蚀性提高。Cu coating was prepared by ultrasonic mechanical plating experimental device;the appearance, bonding strength, surface morphology and chemical composition of the Cu coating were analyzed by scanning electron microscope with aid of energy spectrometer;the corrosion resistance of the Cu coating was also tested. Results showed that the ultrasonic mechanical Cu plated coating was dense with uniform lustre, had good bonding strength and improved corrosion resistance.

关 键 词：超声机械镀铜 结合强度 镀层 耐腐蚀性 

分 类 号：TQ153.2[化学工程—电化学工业]