Research and Application of Wear Resistant Refractories for Cooling Zone of Large Scale Coke Dry Quenching Ovens  

作　　者：XU Guotao SHENG Junbo LYU Yongjin CHEN Shengchun CUI Huiming ZHANG Honglei LIU Li 

机构地区：[1]Wuhan Iron and Steel(Group)Corp.,Wuhan 430080,China

出　　处：《China's Refractories》2017年第2期17-20,共4页中国耐火材料（英文版）

摘　　要：In order to prolong the service life of the cooling zone of large scale coke dry quenching ovens,six kinds possible refractories for the cooling zone of large scale coke dry quenching ovens： SiC containing brick A,SiC containing brick B,mullite-andalusite brick,spinel containing brick,zirconia containing brick,corundum-mullite brick and grade B mullite brick,were analyzed in properties. It is found that the cooling zone lining adopting SiC containing bricks or mullite-andalusite bricks has much longer service life. Based on this,a new type of wear resistant brick was developed. The brick has a compressive strength of 135 MPa,a wear loss of 2. 10cm^3（only a quarter of that of the grade B mullite brick）,and a higher bulk density than the grade B mullite brick. The application of the brick in a 140t·h^（-1）coke dry quenching oven showed that it performed better than the grade B mullite brick. The cooling zone adopting the new bricks has a lower coke discharging temperature,which is beneficial to the enhancement of heat recovery efficiency and steam power generation.In order to prolong the service life of the cooling zone of large scale coke dry quenching ovens,six kinds possible refractories for the cooling zone of large scale coke dry quenching ovens： SiC containing brick A,SiC containing brick B,mullite-andalusite brick,spinel containing brick,zirconia containing brick,corundum-mullite brick and grade B mullite brick,were analyzed in properties. It is found that the cooling zone lining adopting SiC containing bricks or mullite-andalusite bricks has much longer service life. Based on this,a new type of wear resistant brick was developed. The brick has a compressive strength of 135 MPa,a wear loss of 2. 10cm^3（only a quarter of that of the grade B mullite brick）,and a higher bulk density than the grade B mullite brick. The application of the brick in a 140t·h^（-1）coke dry quenching oven showed that it performed better than the grade B mullite brick. The cooling zone adopting the new bricks has a lower coke discharging temperature,which is beneficial to the enhancement of heat recovery efficiency and steam power generation.

关 键 词：coke dry quenching ovens  cooling zone wear resistant mullite -andalusite brick 

分 类 号：TQ175.7[化学工程—硅酸盐工业]