Effect of Andalusite on Properties of Homogenized Bauxite Based Al2O3-SiC-C Castables  

作　　者：ZHANG Ting HAN Bingqiang LI Nan 

机构地区：[1]The State Key Laboratory of Refractories and Metallurgy,Wuhan University of Science and Technology,Wuhan 430081,China

出　　处：《China's Refractories》2017年第2期44-48,共5页中国耐火材料（英文版）

摘　　要：In this study,in order to evaluate the performance of homogenized bauxite,two Al_2O_3-SiC-C castables were prepared using homogenized bauxite and brown fused corundum as aggregates,respectively. 5 mass%andalusite was introduced into the two castables so as to research the effect and mechanism of andalusite in Al_2O_3-SiC-C castables. The results showed that：（1） compared with the brown fused corundum based castables,the homogenized bauxite based castables had higher cold strength after heat treatment,but lower hot modulus of rupture;（2） addition of 5 mass% andalusite could enhance the cold and hot modulus of rupture,improve the thermal shock resistance,and optimize the microstructure of specimens;（ 3） the mullitization of andalusite was not obvious in the castables fired at 1100-1400℃.In this study,in order to evaluate the performance of homogenized bauxite,two Al_2O_3-SiC-C castables were prepared using homogenized bauxite and brown fused corundum as aggregates,respectively. 5 mass%andalusite was introduced into the two castables so as to research the effect and mechanism of andalusite in Al_2O_3-SiC-C castables. The results showed that：（1） compared with the brown fused corundum based castables,the homogenized bauxite based castables had higher cold strength after heat treatment,but lower hot modulus of rupture;（2） addition of 5 mass% andalusite could enhance the cold and hot modulus of rupture,improve the thermal shock resistance,and optimize the microstructure of specimens;（ 3） the mullitization of andalusite was not obvious in the castables fired at 1100-1400℃.

关 键 词：brown fused corundum homogenizedbauxite ANDALUSITE castables for trough 

分 类 号：TQ175.732[化学工程—硅酸盐工业]