High-Temperature Annealing Induced He Bubble Evolution in Low Energy He Ion Implanted 6H-SiC  

作　　者：刘玉柱 李炳生 张莉 

机构地区：[1]Jiangsu Collaborative Innovation Center on Atmospheric Environment and Equipment Technology(CICAEET),Nanjing University of Information Science&Technology,Nanjing 210044 [2]Institute of Modern Physics,Chinese Academy of Sciences,Lanzhou 730000 [3]Department of Physics,School of Science,Lanzhou University of Technology,Lanzhou 730050

出　　处：《Chinese Physics Letters》2017年第5期40-43,共4页中国物理快报（英文版）

基　　金：Supported by the National Natural Science Foundation of China under Grant No 11475229

摘　　要：Bubble evolution in low energy and high dose He-implanted 6H-SiC upon thermal annealing is studied. The （0001）-oriented 6H-SiC wafers are implanted with 15keV helium ions at a dose of 1×10^17 cm^-2 at room temperature. The samples with post-implantation are annealed at temperatures of 1073, 1173, 1273, and 1473K for 30rain. He bubbles in the wafers are examined via cross-sectional transmission electron microscopy （XTEM） analysis. The results present that nanoscale bubbles are almost homogeneously distributed in the damaged layer of the as-implanted sample, and no significant change is observed in the He-implanted sample after 1073 K annealing. Upon 1193 K annealing, almost full recrystallization of He-implantation-induced amorphization in 6H-SiC is observed. In addition, the diameters of He bubbles increase obviously. With continually increasing temperatures to 1273K and 1473 K, the diameters of He bubbles increase and the number density of lattice defects decreases. The growth of He bubbles after high temperature annealingabides by the Ostwald ripening mechanism. The mean diameter of He bubbles located at depths of 120-135 nm as a function of annealing temperature is fitted in terms of a thermal activated process which yields an activation energy of 1.914＋0.236eV.Bubble evolution in low energy and high dose He-implanted 6H-SiC upon thermal annealing is studied. The （0001）-oriented 6H-SiC wafers are implanted with 15keV helium ions at a dose of 1×10^17 cm^-2 at room temperature. The samples with post-implantation are annealed at temperatures of 1073, 1173, 1273, and 1473K for 30rain. He bubbles in the wafers are examined via cross-sectional transmission electron microscopy （XTEM） analysis. The results present that nanoscale bubbles are almost homogeneously distributed in the damaged layer of the as-implanted sample, and no significant change is observed in the He-implanted sample after 1073 K annealing. Upon 1193 K annealing, almost full recrystallization of He-implantation-induced amorphization in 6H-SiC is observed. In addition, the diameters of He bubbles increase obviously. With continually increasing temperatures to 1273K and 1473 K, the diameters of He bubbles increase and the number density of lattice defects decreases. The growth of He bubbles after high temperature annealingabides by the Ostwald ripening mechanism. The mean diameter of He bubbles located at depths of 120-135 nm as a function of annealing temperature is fitted in terms of a thermal activated process which yields an activation energy of 1.914＋0.236eV.

关 键 词：High-Temperature Annealing Induced He Bubble Evolution in Low Energy He Ion Implanted 6H-SiC HRTEM 

分 类 号：TG156.2[金属学及工艺—热处理]