TRIP800钢板Q＆P处理后的疲劳性能研究  

Research on Fatigue Property of TRIP800 Steel Plate after Q&P Treatment

作　　者：陈立伟[1] 颜景润[1] 倪笑宇 王烁[1] 李欣[1] 

机构地区：[1]河北建筑工程学院机械工程学院,河北张家口075000

出　　处：《热加工工艺》2017年第12期205-207,211,共4页Hot Working Technology

基　　金：2014年度河北建筑工程学院校级科研基金项目(QN201401)

摘　　要：采用最小应力/最大应力σ_(min)/σ_(max)≈0的拉-拉循环加载,测定了TRIP钢经Q&P处理后的疲劳应力-循环次数(S-N)曲线。并对所得的试验数据进行了拟合处理。结果表明:TRIP钢经Q&P处理后在加载频率8Hz、应力比R≈0时的S-N曲线的拟合公式为:lgN=42.062-15.026lgσ(N为循环周次;σ为最大循环应力σ_(max));TRIP800钢板经过Q&P处理后疲劳源在表面下的第二相处,裂纹的扩展区为微孔聚集型断裂,而瞬断区为典型的脆性断裂。Fatigue stress cycle times （S-N） curve of TRIP800 steel after Q＆P treatment was measured by using pulling- pulling cyclic loading of minimum stress/maximum stress σmin/σmx≈0. The experimental data were fitted. The results show that fitting formula of S-N curve of TRIP steel after Q＆P treatment during loading frequency of 8Hz and stress ratio R ≈ 0 is lgN=42.062-15.0261gtr （N is cycle times; σ is maximum cyclic stress σmax）; after Q＆P treatment, the fatigue source of TRIP800 steel plate is in the second phase under the surface, the crack propagation zone is a micro-porous aggregate fracture, and the transient breaking zone is a typical brittle fracture.

关 键 词：TRIP钢板 应力-循环次数(S-N)曲线 疲劳断裂 断口扫描 

分 类 号：TG156.31[金属学及工艺—热处理] TG113.255[金属学及工艺—金属学]