单晶Cu等通道转角挤压A路径形变特征及力学性能  

Deformation Characteristics and Mechanical Properties of Single Crystal Copper During Equal Channel Angular Pressing by Route A

作　　者：郭廷彪[1,2] 李琦[1] 王晨[1] 张锋[1] 贾智[1,2] GUO Tingbiao LI Qi WANG Chen ZHANG Feng JIA Zhi(State Key Laboratory of Advanced Processing and Recycling of Nonferrous Metals, Lanzhou University of Technology, Lanzhou 730050, China Key Laboratory of Non-Ferrous Metal Alloys and Processing, Ministry of Education, Lanzhou University of Technology, Lanzhou 730050, China)

机构地区：[1]兰州理工大学省部共建有色金属先进加工与再利用国家重点实验室,兰州730050 [2]兰州理工大学有色金属合金及加工教育部重点实验室,兰州730050

出　　处：《金属学报》2017年第8期991-1000,共10页Acta Metallurgica Sinica

基　　金：国家自然科学基金项目No.51261016~~

摘　　要：采用XRD、EBSD和TEM技术对单晶高纯Cu(99.999%)经等通道转角挤压(ECAP)A路径过程中的形变织构进行了研究,测试了ECAP后单晶Cu的力学性能和导电性能,并分析了变形过程中织构演变机理及其对力学性能和导电性能的影响。结果表明:原始单晶Cu经2道次变形后,晶内出现了微小的等轴状形变结构;4道次变形后,形成了(110)取向一致的形变带结构;8道次变形后,单晶组织开始破碎,晶粒取向又逐渐趋于(111)面,形成了{111}<110>和{111}<112>织构及较弱的{001}<100>再结晶织构。中、低应变下,形成稳定取向的{hkl}<110>织构,可有效降低晶界对电子的散射作用,使电导率略有增加,同时有利于大幅度提高材料的加工硬化率。单晶Cu变形初始阶段形成了大量小角度晶界,随着应变的增加,小角度晶界逐渐向大角度晶界转变。由于变形过程中位错积聚及晶界密度增加对位错运动起到阻碍作用,3道次变形后,抗拉强度从168 MPa增加至400 MPa,延伸率从63%减小至27.3%,在随后的变形中抗拉强度增加缓慢,延伸率略有回升。前8道次变形中硬度不断增加,8道次变形后出现了再结晶,导致随后的挤压过程中硬度不稳定。The single crystal copper has got more and more attention in the important areas of the national economy due to its good conductivity and thermal conductivity and elongation. Whereas the low- er strength limits its application and strengthening methods of single crystal copper are of great concern. The traditional strengthening methods, such as solid solution strengthening, fine grain strengthening and deformation strengthening, can seriously damage the conductivity of single crystal copper. As an effective method for severe plastic deformation （SPD）, equal channel angular pressing （ECAP） can effectively improve the material strength and keep its excellent performance by controlling the deformation and strain.Deformation texture of the single crystal copper （99.999%） during ECAP by A route was investigated by XRD, EBSD and TEM, the mechanical properties and conductivity were tested, and the mechanism of texture evolution and influence factors of mechanical and electrical properties during deformation pro- cess were analyzed. The results show that equiaxed deformation structure with small sizes appeared in single crystal copper after two passes extruded. After four passes of deformation, deformation band struc- ture with same （110） orientation was formed. And the grain orientation of the highly refined grains gradual- ly tended to the （111 ） surface, the {111 }〈 110〉, {111 }〈 112〉 textu res and the little {001 }〈 100〉 recrystalliza- tion texture formed. The scattering of electrons by grain boundaries （GBs） can effectively get reduced and conductivity increases slightly, at the same time, the work hardening rate of the material is significant- ly improved when {hk/}〈110〉 texture with stable orientation forms under medium and low strains. A large number of low-angle grain boundaries （LAGBs） are formed in the initial deformation stage of single crys- tal copper. With the increase of strain, the LAGBs gradually change to the high-angle grain boundaries （HAGBs）. Dislocati

关 键 词：单晶Cu 等通道转角挤压 形变带 织构 力学性能 