Advanced Electro-active Dry Adhesive Actuated by an Artificial Muscle Constructed from an Ionic Polymer Metal Composite Reinforced with Nitrogen-doped Carbon Nanocages  

作　　者：Qingsong He Xu Yang Zhongyuan Wang Jin Zhao Min Yu Zhen Hu Zhendong Dai 

机构地区：[1]Institute of Bio-inspired Structure and Surface Engineering, Jiangsu Provincial Key Laboratory of Bionic Functional Materials, Col- lege of Astronautics, Nanjing University of Aeronautics & Astronautics, Nanjing 210016, China [2]College of Mechanical and Electrical Engineering Nanjing University of Aeronautics & Astronautics, Nanjing 210016, China [3]Key Laboratory of Mesoscopic Chemistry of MOE, Jiangsu Provincial Lab for Nanotechnology, School of Chemistry and Chemical Engineering, Nanjing University, Nanjing 210093, China

出　　处：《Journal of Bionic Engineering》2017年第3期567-578,共12页仿生工程学报（英文版）

基　　金：This work was partially supported by the National Natural Science Foundation of China （Grant Nos. 51605220, U1637101, 51435008）, the Natural Science Foundation of Jiangsu Province （Grant No. BK20160793）, the High Level Introduction of Talent Research Start-up Fund in NUAA （Grant No. 1011-YAH16010）, and Open Project Fund in Jiangsu Provincial Key Laboratory for Interventional Medical Devices （Grant No. jr1601）. The authors would very much like to thank Professor Stanislav N. Gorb in the Department of Functional Morphology and Biome- chanics in the Zoological Institute of the University of Kiel, Germany, for his help with the mushroom-shapeddry adhesives, and also thank Dr. Yajun Xue and Miss Yan Ding for help with the SEM observations.

摘　　要：An advanced electro-active dry adhesive, which was composed of a mushroom-shaped tibrillar dry adhesive array actuated by an Ionic Polymer Metal Composite （IPMC） artificial muscle reinforced with nitrogen-doped carbon nanocages （NCNCs）, was developed to imitate the actuation of a gecko＇s toe. The properties of the NCNC-reinforced Nation membrane, the electro- mechanical properties of the NCNC-reinforced IPMC, and the related electro-active adhesion ability were investigated. The NCNCs were uniformly dispersed in the 0.1 wt% NCNC/Nafion membrane, and there was a seamless connection with no clear interface between the dry adhesive and the IPMC. Our 0.1 wt% NCNC/Nation-IPMC actuator shows a displacement and force that are 1.6 - 2 times higher than those of the recast Nafion-IPMC. This is due to the increased water uptake （25.39%） and tensile strength （24.5 MPa） of the specific 3D hollow NCNC-reinforced Nation membrane, as well as interactions between the NCNCs and the sulfonated groups of the Nation. The NCNC/Nation-IPMC was used to effectively actuate the mushroom-shaped dry adhesive. The normal adhesion forces were 7.85 raN, 12.1 mN, and 51.7 mN at sinusoidal voltages of 1.5 V, 2.5 V, and 3.5 V, respectively, at 0.1 Hz. Under the bionic leg trail, the normal and shear forces were approximately 713.5 mN （159 mN·cm^-2） and 1256.6 mN （279 mN·cm^-2）, respectively, which satisfy the required adhesion. This new electro-active dry adhesive can be applied for active, distributed actuation and flexible grip in robots.An advanced electro-active dry adhesive, which was composed of a mushroom-shaped tibrillar dry adhesive array actuated by an Ionic Polymer Metal Composite （IPMC） artificial muscle reinforced with nitrogen-doped carbon nanocages （NCNCs）, was developed to imitate the actuation of a gecko＇s toe. The properties of the NCNC-reinforced Nation membrane, the electro- mechanical properties of the NCNC-reinforced IPMC, and the related electro-active adhesion ability were investigated. The NCNCs were uniformly dispersed in the 0.1 wt% NCNC/Nafion membrane, and there was a seamless connection with no clear interface between the dry adhesive and the IPMC. Our 0.1 wt% NCNC/Nation-IPMC actuator shows a displacement and force that are 1.6 - 2 times higher than those of the recast Nafion-IPMC. This is due to the increased water uptake （25.39%） and tensile strength （24.5 MPa） of the specific 3D hollow NCNC-reinforced Nation membrane, as well as interactions between the NCNCs and the sulfonated groups of the Nation. The NCNC/Nation-IPMC was used to effectively actuate the mushroom-shaped dry adhesive. The normal adhesion forces were 7.85 raN, 12.1 mN, and 51.7 mN at sinusoidal voltages of 1.5 V, 2.5 V, and 3.5 V, respectively, at 0.1 Hz. Under the bionic leg trail, the normal and shear forces were approximately 713.5 mN （159 mN·cm^-2） and 1256.6 mN （279 mN·cm^-2）, respectively, which satisfy the required adhesion. This new electro-active dry adhesive can be applied for active, distributed actuation and flexible grip in robots.

关 键 词：electro-active dry adhesive bionic ionic polymer metal composite Nation membrane carbon nanocage 

分 类 号：TP24[自动化与计算机技术—检测技术与自动化装置] TE357.46[自动化与计算机技术—控制科学与工程]