环氧建筑结构胶冬季施工性能研究  

Research on properties of epoxy building structural adhesive used in winter

作　　者：韩煜[1] 王玉卓[1] 姚源渊 

机构地区：[1]河南工业职业技术学院,河南南阳473009

出　　处：《新型建筑材料》2017年第8期22-25,53,共5页New Building Materials

摘　　要：在-5℃条件下,研究了促进剂(DMP-30)、气相白炭黑、水泥、硅粉、石棉纤维及偶联剂用量对6002环氧胶粘剂适用期、流淌性能、力学性能的影响,制备了冬季低温施工条件下无需加热配胶,早期(1 d)抗压强度高的环氧建筑结构胶。试验结果表明:当m(6002环氧树脂)∶m(593固化剂)∶m(DMP-30促进剂)∶m(KH-550硅烷偶联剂)∶m(气相白炭黑)∶m(水泥)∶m(硅粉)∶m(石棉纤维)=100∶25∶1∶5∶1∶95∶95∶10时,制备的环氧建筑结构胶性能最优。适用期为90 min,触变性好、不挂流;1 d、14 d抗压强度分别为45、85MPa,14 d抗拉强度为35 MPa,正拉粘结强度为4.5 MPa(且为混凝土内聚破坏),符合GB 50728—2011对建筑结构胶的性能要求。The novel epoxy building structural adhesive with high compressive strength of early stage （1 d） amd no need of pre-heating before used at winter low temperature was prepared. Effect of the dosage of accelerator （DMP-30）,fumed silica,ce- ment,silicon powder, asbestos fiber and coupling agent on the working time, thixotropy, and mechanical properties of the 6002 epoxy adhesive under -5 ~C condition was studied. Results show that the adhesive acquires its best properties when the mass ratio of 6002 epoxy resin, curing agent （593）, accelerator （DMP-30）, coupling agent （KH-550）,fumed silica, cement, silicon powder and as- bestos fiber is 100：25：1：5：1：95：95：10. Its working time is 90 min, thixotropy is good, no sagging phenomenon appears, its compressive strength of ld and 14 d is 45 MPa and 85 MPa respectively,its 14 d tensile strength is 35 MPa, and its bonding strength to con- crete is 4.5 MPa,the failure mode was concrete cohesion failure. The prepared adhesive completely meets the property requirements in standard GB 50728-2011.

关 键 词：环氧树脂 结构胶 低温 早强 

分 类 号：TU581.3[建筑科学—建筑技术科学]