聚丙烯酸作用下皮胶原纤维不同尺度结构的变化研究(续)  

Effects of polyacrylic acid on different scales of leather collagen fibers

作　　者：邹祥龙[1] 柴玉叶[1] 许晓红[1] 兰云军[1] 

机构地区：[1]温州大学浙江省皮革工程重点实验室,浙江温州325027

出　　处：《中国皮革》2017年第9期22-25,32,共5页China Leather

基　　金：温州大学浙江省重中之重学科开放基金(100061200147)

摘　　要：采用透射电子显微镜、扫描电子显微镜和应力-应变分析对湿态和干态聚丙烯酸(PAA)复鞣革不同尺度结构进行了表征。结果表明:PAA主要在介孔和大孔结构层次与胶原纤维作用,在充水状态下,PAA对胶原纤维的聚集结构无明显影响,但在湿-干态转变过程中显著影响胶原纤维的聚集行为,使胶原纤维间的作用力及胶原纤维聚集的有序程度降低。The different scales structure of leather retanned with polyacrylic acid （PAA） under dry and wet state was characterized by transmission electron microscopy （TEM）, scanning electron microscope （SEM） and stress-strain analysis. The results show that PAA mainly interacts with collagen fibers at the level of mesoporous and macro-porous structure and has little influence on the aggregation structure of collagen fibers before drying. During the wetdry state transition PAA has significant effect on the collagen fibers aggregation with making the interaction force and the aggregation degree of collagen decreasing.

关 键 词：聚丙烯酸 胶原纤维 聚集结构 湿-干态转变 取向程度 

分 类 号：TS512[轻工技术与工程—皮革化学与工程]