Acid/Base Treatment of Monolithic Activated Carbon for Coating Silver with Tunable Morphology  

作　　者：程辞 WANG Fei 赵斌元 宁月生 LAI Yijian WANG Lei 

机构地区：[1]State Key Laboratory of Metal Matrix Composites, School of Materials Science and Engineering, Shanghai Jiao Tong University, Shanghai 200240, China [2]Green Support Materials Technologies (Shanghai) Co. Ltd., Shanghai 200240, China

出　　处：《Journal of Wuhan University of Technology(Materials Science)》2017年第4期760-765,共6页武汉理工大学学报（材料科学英文版）

基　　金：Funded by the Interdisciplinary Program of Shanghai Jiao Tong University(YG2016MS24)

摘　　要：Silver coatings on the exterior surface of monolithic activated carbon（MAC） with different morphology were prepared by directly immersing MAC into [Ag（NH3）2]NO3 solution. Acid and base treatments were employed to modify the surface oxygenic groups of MAC, respectively. The MACs＇ Brunauer-EmmettTeller（BET） surface area, surface groups, and silver coating morphology were characterized by N2 adsorption, elemental analysis（EA）, X-ray photoelectron spectroscopy（XPS）, and scanning electron microscopy（SEM）, respectively. The coating morphology was found to be closely related to the surface area and surface functional groups of MAC. For a raw MAC which contained a variety of oxygenic groups, HNO3 treatment enhanced the relative amount of highly oxidized groups such as carboxyl and carbonates, which disfavored the deposition of silver particles. By contrast, Na OH treatment significantly improved the amount of carbonyl groups, which in turn improved the deposition amount of silver. Importantly, lamella silver was produced on raw MAC while Na OH treatment resulted in granular particles because of the capping effect of carbonyl groups. At appropriate [Ag（NH3）2]NO3 concentrations, silver nanoparticles smaller than 100 nm were homogeneously dispersed on Na OH-treated MAC. The successful tuning of the size and morphology of silver coatings on MAC is promising for novel applications in air purification and for antibacterial or aesthetic purposes.Silver coatings on the exterior surface of monolithic activated carbon（MAC） with different morphology were prepared by directly immersing MAC into [Ag（NH3）2]NO3 solution. Acid and base treatments were employed to modify the surface oxygenic groups of MAC, respectively. The MACs＇ Brunauer-EmmettTeller（BET） surface area, surface groups, and silver coating morphology were characterized by N2 adsorption, elemental analysis（EA）, X-ray photoelectron spectroscopy（XPS）, and scanning electron microscopy（SEM）, respectively. The coating morphology was found to be closely related to the surface area and surface functional groups of MAC. For a raw MAC which contained a variety of oxygenic groups, HNO3 treatment enhanced the relative amount of highly oxidized groups such as carboxyl and carbonates, which disfavored the deposition of silver particles. By contrast, Na OH treatment significantly improved the amount of carbonyl groups, which in turn improved the deposition amount of silver. Importantly, lamella silver was produced on raw MAC while Na OH treatment resulted in granular particles because of the capping effect of carbonyl groups. At appropriate [Ag（NH3）2]NO3 concentrations, silver nanoparticles smaller than 100 nm were homogeneously dispersed on Na OH-treated MAC. The successful tuning of the size and morphology of silver coatings on MAC is promising for novel applications in air purification and for antibacterial or aesthetic purposes.

关 键 词：monolithic activated carbon silver coating morphology functional groups surface modification 

分 类 号：TQ424.1[化学工程]