Road Performances of Mesoporous Nano-silica Modified Asphalt Binders  

作　　者：刘小明 cao fengjie wang lei tao ruwei li tingyu 

机构地区：[1]School of Civil Engineering, Central South University, Changsha 410075, China

出　　处：《Journal of Wuhan University of Technology(Materials Science)》2017年第4期845-853,共9页武汉理工大学学报（材料科学英文版）

基　　金：Funded by the China Scholarship Council(201506375019)

摘　　要：The objective of this paper was to find new modifier to improve the aging resistance and low temperature cracking resistance of asphalt. To investigate the aging resistance of modified asphalt binders, mesoporous nano-silica（doping Ti^（4＋）） was used as a asphalt modifier. Some physical properties including penetration, ductility, and softening point of asphalt were analyzed with RTFO（Rotating thin film oven） aging and ultraviolet aging. Moreover, the performances of high and low temperature of modified asphalt binders with pressure aging were tested by dynamic shear rheometer（DSR） test and bending beam rheometer（BBR） test. These results showed that the penetration decreased, low temperature ductility, and softening point increased when adding mesoporous nano-silica to base asphalt. After ultraviolet radiation aging, the penetration loss and ductility loss of modified asphalt decreased than that of original asphalt, the increase of softening point was also significantly reduced than that of base asphalt. Furthermore, The test results of DSR and BBR showed that the G＊sinδ and creep modulus‘s＇ of pressure aged asphalt decreased, but the creep rate ‘m＇ increased. It can be concluded that the aging resistance and cracking resistance of modified asphalt are improved by adding mesoporous nano-silica, especially the doping of Ti^（4＋） could improve the aging resistance obviously.The objective of this paper was to find new modifier to improve the aging resistance and low temperature cracking resistance of asphalt. To investigate the aging resistance of modified asphalt binders, mesoporous nano-silica（doping Ti^（4＋）） was used as a asphalt modifier. Some physical properties including penetration, ductility, and softening point of asphalt were analyzed with RTFO（Rotating thin film oven） aging and ultraviolet aging. Moreover, the performances of high and low temperature of modified asphalt binders with pressure aging were tested by dynamic shear rheometer（DSR） test and bending beam rheometer（BBR） test. These results showed that the penetration decreased, low temperature ductility, and softening point increased when adding mesoporous nano-silica to base asphalt. After ultraviolet radiation aging, the penetration loss and ductility loss of modified asphalt decreased than that of original asphalt, the increase of softening point was also significantly reduced than that of base asphalt. Furthermore, The test results of DSR and BBR showed that the G＊sinδ and creep modulus‘s＇ of pressure aged asphalt decreased, but the creep rate ‘m＇ increased. It can be concluded that the aging resistance and cracking resistance of modified asphalt are improved by adding mesoporous nano-silica, especially the doping of Ti^（4＋） could improve the aging resistance obviously.

关 键 词：mesoporous nano-silica（MNS） dynamic shear rheometer bending beam rheometer aging resistance 

分 类 号：U414[交通运输工程—道路与铁道工程]