高强高贝利特硅酸盐水泥熟料矿相匹配研究  

Preparation of high strength high belite portland cement clinker

作　　者：高显束 王晶[1] 王敏[1] 张坤悦[1] 

机构地区：[1]中国建筑材料科学研究总院,北京100024

出　　处：《中国建材科技》2017年第4期32-33,共2页China Building Materials Science & Technology

基　　金：国家"十二五"科技支撑计划(课题编号:2014BAE05B01)

摘　　要：本文基于水泥工业节能减排的需求,通过高强高贝利特硅酸盐水泥熟料的低钙组成设计,针对硅酸盐水泥熟料中不同矿物具有的不同性能特点,制备出高强高贝利特硅酸盐水泥熟料,实现熟料CaO-SiO_2-Al_2O_3-Fe_2O_3多元体系的矿相组成优化匹配,达到实现低钙组成和高强度高性能的目的,降低水泥制备过程的碳排放和能源消耗。This article is based on the demand for cement industrial energy conservation and emissions reduction,through with high strength and high bailey,of low calcium silicate cement clinker design, aiming at different minerals in Portland cement clinker with different performance characteristics,to prepare a kind of Portland cement clinker with high strength and high C_2S content,to realize the clinker CaO-SiO_2-Al_2O_3-Fe_2O_3 composition optimization matching of multivariate system,thus achieving the purpose of the implementation of low calcium and high strength and high performance,and reducing carbon emissions and energy consumption of cement preparation process.

关 键 词：高强高贝利特 熟料 矿相匹配 

分 类 号：TQ172.7[化学工程—水泥工业]