Effect of Post-weld Heat Treatment on Mechanical Characteristics of AZ31 Magnesium Alloy Welded Joints  

作　　者：闫志峰 张红霞 DUAN Jinwen LIU Fei WANG Guilei 

机构地区：[1]College of Materials Science and Engineering, Taiyuan University of Technology, Taiyuan 030024, China [2]Shanxi Key Laboratory of Advanced Magnesium-based Materials, Taiyuan 030024, China

出　　处：《Journal of Wuhan University of Technology(Materials Science)》2017年第5期1205-1212,共8页武汉理工大学学报（材料科学英文版）

基　　金：Funded by the National Natural Science Foundation of China(Nos.51505322,51175364);Natural Science Foundation of Shanxi Province of China(No.2013011014-3)

摘　　要：Tungsten inert gas（TIG） welding was performed on 2.7 mm thick commercial extruded AZ31 B magnesium alloy plates. We investigated the effect of post-weld heat treatment（PWHT） on the microstructure, mechanical properties and precipitated phase of the weld joints. The results showed that during the annealing treatment（200 ℃-1 h, 250 ℃-1 h, 300 ℃-1 h, 350 ℃-1 h, 400 ℃-1 h, and 450 ℃-1 h）, the average grain size in the weld seam was the minimum after annealing at 400 ℃ for 1 hour, and then abnormally grew up after annealing at 450 ℃ for 1 hour. The mechanical properties enhanced when the joints were processed from 200 ℃-1 h to 400 ℃-1 h but sharply decreased with increasing annealing temperature. In contrast to the annealing treatment, solution treatment（250 ℃-10 h, 300 ℃-10 h, 350 ℃-10 h, 400 ℃-10 h, and 450 ℃-10 h） exhibited a better ductility but a slight deterioration in tensile strength. Especially speaking, no eutectic compounds（such as Mg17 Al12） were observed in the weld seam. The supersaturated Al atoms were precipitated in a coarse spherical shape dispersed in the weld seam. The precipitated Al atoms dissolved in the matrix substances at the condition（400 ℃-1 h） or（250 ℃-10 h）. The solution treatment caused grain coarsening and precipitated Al atoms dissolved in the weld seam substantially, which resulted in a drop in micro-hardness at the weld seam compared to the area of the annealed joints.Tungsten inert gas（TIG） welding was performed on 2.7 mm thick commercial extruded AZ31 B magnesium alloy plates. We investigated the effect of post-weld heat treatment（PWHT） on the microstructure, mechanical properties and precipitated phase of the weld joints. The results showed that during the annealing treatment（200 ℃-1 h, 250 ℃-1 h, 300 ℃-1 h, 350 ℃-1 h, 400 ℃-1 h, and 450 ℃-1 h）, the average grain size in the weld seam was the minimum after annealing at 400 ℃ for 1 hour, and then abnormally grew up after annealing at 450 ℃ for 1 hour. The mechanical properties enhanced when the joints were processed from 200 ℃-1 h to 400 ℃-1 h but sharply decreased with increasing annealing temperature. In contrast to the annealing treatment, solution treatment（250 ℃-10 h, 300 ℃-10 h, 350 ℃-10 h, 400 ℃-10 h, and 450 ℃-10 h） exhibited a better ductility but a slight deterioration in tensile strength. Especially speaking, no eutectic compounds（such as Mg17 Al12） were observed in the weld seam. The supersaturated Al atoms were precipitated in a coarse spherical shape dispersed in the weld seam. The precipitated Al atoms dissolved in the matrix substances at the condition（400 ℃-1 h） or（250 ℃-10 h）. The solution treatment caused grain coarsening and precipitated Al atoms dissolved in the weld seam substantially, which resulted in a drop in micro-hardness at the weld seam compared to the area of the annealed joints.

关 键 词：magnesium alloy welded joint heat treatments microstructure mechanical properties 

分 类 号：TG441.8[金属学及工艺—焊接]