Enhancement of electroluminescent properties of organic optoelectronic integrated device by doping phosphorescent dye  

作　　者：雷疏影 钟建 周殿力 朱方云 邓朝旭 

机构地区：[1]State Key Laboratory of Electronic Thin Films and Integrated Devices [2]School of Optoelectronic Information, University of Electronic Science and Technology of China (UESTC)

出　　处：《Chinese Physics B》2017年第11期434-440,共7页中国物理B（英文版）

基　　金：Project supported by the National Natural Science Foundation of China(Grant No.61675041);the National Science Funds for Creative Research Groups of China(Grant No.61421002)

摘　　要：Organic optoelectronic integrated devices（OIDs） with ultraviolet（UV） photodetectivity and different color emitting were constructed by using a thermally activated delayed fluorescence（TADF） material 4, 5-bis（carbazol-9-yl）-1, 2-dicyanobenzene（2 CzPN） as host. The OIDs doping with typical red phosphorescent dye [tris（1-phenylisoquinoline）iridium（Ⅲ）, Ir（piq）3], orange phosphorescent dye {bis[2-（4-tertbutylphenyl）benzothiazolato-N,C-（2＇）]iridium（acetylacetonate）,（tbt）2 Ir（acac）}, and blue phosphorescent dye [bis（2, 4-di-fluorophenylpyridinato）-tetrakis（1-pyrazolyl）borate iridium（Ⅲ）, FIr6] were investigated and compared. The（tbt）2 Ir（acac）-doped orange device showed better performance than those of red and blue devices, which was ascribed to more effective energy transfer. Meanwhile, at a low dopant concentration of 3 wt.%, the（tbt）2 Ir（acac）-doped OIDs showed the maximum luminance, current efficiency, power efficiency of 70786 cd/m^2, 39.55 cd/A, and 23.92 lm/W, respectively, and a decent detectivity of 1.07 × 10^11 Jones at a bias of -2 V under the UV-350 nm illumination. This work may arouse widespread interest in constructing high efficiency and luminance OIDs based on doping phosphorescent dye.Organic optoelectronic integrated devices（OIDs） with ultraviolet（UV） photodetectivity and different color emitting were constructed by using a thermally activated delayed fluorescence（TADF） material 4, 5-bis（carbazol-9-yl）-1, 2-dicyanobenzene（2 CzPN） as host. The OIDs doping with typical red phosphorescent dye [tris（1-phenylisoquinoline）iridium（Ⅲ）, Ir（piq）3], orange phosphorescent dye {bis[2-（4-tertbutylphenyl）benzothiazolato-N,C-（2＇）]iridium（acetylacetonate）,（tbt）2 Ir（acac）}, and blue phosphorescent dye [bis（2, 4-di-fluorophenylpyridinato）-tetrakis（1-pyrazolyl）borate iridium（Ⅲ）, FIr6] were investigated and compared. The（tbt）2 Ir（acac）-doped orange device showed better performance than those of red and blue devices, which was ascribed to more effective energy transfer. Meanwhile, at a low dopant concentration of 3 wt.%, the（tbt）2 Ir（acac）-doped OIDs showed the maximum luminance, current efficiency, power efficiency of 70786 cd/m^2, 39.55 cd/A, and 23.92 lm/W, respectively, and a decent detectivity of 1.07 × 10^11 Jones at a bias of -2 V under the UV-350 nm illumination. This work may arouse widespread interest in constructing high efficiency and luminance OIDs based on doping phosphorescent dye.

关 键 词：organic optoelectronic integrated device thermally activated delayed fluorescence host phosphorescent dye high luminance 

分 类 号：TN383.1[电子电信—物理电子学] TB383[一般工业技术—材料科学与工程]