K_2O·nSiO_2基无机复合防火玻璃的试验研究  

Experimental Investigation on Inorganic Composite K_2O·nSiO_2 Based Flame-proof Glass

作　　者：杨晨[1] 张文玲[1] 梁中生[1] 

机构地区：[1]秦皇岛玻璃工业研究设计院,秦皇岛市066004

出　　处：《玻璃》2017年第11期11-14,共4页Glass

基　　金：国家重点研发计划课题2016YFB0303900;秦皇岛市科技计划项目201701B006资助

摘　　要：用纳米SiO_2、氢氧化钾、分散剂制备高模数K_2O·nSiO_2,用氟硅酸钠作为固化剂,将其灌注于2片玻璃中制成防火玻璃样品,可见光透过率75%左右,防火时间大于90min。High modulus K2O·nSiO2 was prepared with nano-meter SiO2 , potassium hydroxide and dispersion agent. The sodium fluosilicate was used as curing agent and was poured into the space between two pieces of glass . The finished flame-proof glass exhibits about 75 % of visible transmittance and more than 90 minutes of the fire-resistance period .

关 键 词：K2O·nSiO2 基无机复合防火液 分散剂 固化剂 

分 类 号：TQ171[化学工程—玻璃工业]