β-Nickel hydroxide cathode material for nano-suspension redox flow batteries  

作　　者：Yue LI Cheng HE Javier PARRONDO Vijay RAMANI Elena V. TIMOFEEVA Yujia DING Carlo SEGRE 

机构地区：[1]Center for Solar Energy and Energy Storage, Department of Energy, Environmental and Chemical Engineering, Washington University in St. Louis, 1 Brookings Dr., St. Louis, MO 63130, USA [2]Physics Department, Illinois Institute of Technology, Chicago, IL 60616, USA

出　　处：《Frontiers in Energy》2017年第3期401-409,共9页能源前沿（英文版）

摘　　要：As part of an effort to build a prototype flow battery system using a nano-suspension containing β-Ni（OH）2 nanoparticles as the cathode material, nano-sized β-Ni（OH）2 particles with well-controlled particle size and morphology were synthesized via the one-step precipitation of a NiCl2 precursor. The composition and morphology of the nanoparticles were characterized by scanning electronic microscopy （SEM） and X-ray diffraction （XRD）. The XRD patterns confirmed that β-Ni（OH）2 was successfully synthesized, while SEM results showed that the particle sizes range from 70 to 150 nm. To ensure that Ni（OH）2 could be employed in the nano-suspension flow battery, the electrochemical performance of the synthesized 13-Ni（OH）2 was initially tested in pouch cells through charge/discharge cycling. The phase transformations occurring during charge/discharge were investigated using in-situ X-ray absorption spectroscopy to obtain the shift in the oxidation state of Ni （X-ray adsorption near edge structure, XANES） and the distances between Ni and surrounding atoms in charged and discharged states （extended X-ray absorption fine structure, EXAFS）. XANES results indicated that the electrode in the discharged state was a mixture of phases because the edge position did not shift back completely. XAFS results further proved that the discharge capacity was provided by β-NiOOH and the ratio between β-Ni（OH）2 and γ-NiOOH in the electrode in the discharged state was 71：29. Preliminary nano-suspension tests in a lab-scale cell were conducted to understand the behavior of the nano-suspension during charge/discharge cycling and to optimize the operating conditions.As part of an effort to build a prototype flow battery system using a nano-suspension containing β-Ni（OH）2 nanoparticles as the cathode material, nano-sized β-Ni（OH）2 particles with well-controlled particle size and morphology were synthesized via the one-step precipitation of a NiCl2 precursor. The composition and morphology of the nanoparticles were characterized by scanning electronic microscopy （SEM） and X-ray diffraction （XRD）. The XRD patterns confirmed that β-Ni（OH）2 was successfully synthesized, while SEM results showed that the particle sizes range from 70 to 150 nm. To ensure that Ni（OH）2 could be employed in the nano-suspension flow battery, the electrochemical performance of the synthesized 13-Ni（OH）2 was initially tested in pouch cells through charge/discharge cycling. The phase transformations occurring during charge/discharge were investigated using in-situ X-ray absorption spectroscopy to obtain the shift in the oxidation state of Ni （X-ray adsorption near edge structure, XANES） and the distances between Ni and surrounding atoms in charged and discharged states （extended X-ray absorption fine structure, EXAFS）. XANES results indicated that the electrode in the discharged state was a mixture of phases because the edge position did not shift back completely. XAFS results further proved that the discharge capacity was provided by β-NiOOH and the ratio between β-Ni（OH）2 and γ-NiOOH in the electrode in the discharged state was 71：29. Preliminary nano-suspension tests in a lab-scale cell were conducted to understand the behavior of the nano-suspension during charge/discharge cycling and to optimize the operating conditions.

关 键 词：nano-suspension flow battery β-Ni（OH）2 scanning electronic microscopy （SEM） X-ray diffraction（XRD） X-ray adsorption near edge structure （XANES） extended X-ray absorption fine structure （EXAFS） 

分 类 号：O614.83[理学—无机化学] TB383[理学—化学]