Role of fragmentation in as-cast structure:numerical study and experimental validation  

作　　者：Yong-jian Zheng Meng-huai Wu A.Kharicha A.Ludwig 

机构地区：[1]Chair of Simulation and Modelling of Metallurgical Processes, Montanuniversitaet Leoben [2]Christian Doppler Laboratory for Advanced Process Simulation of Solidification and Melting, Department of Metallurgy, University of Leoben

出　　处：《China Foundry》2017年第5期321-326,共6页中国铸造（英文版）

基　　金：supported by the Austrian Research Promotion Agency(FFG)through the project of Bridge Early Stage(No.842441);technically supported by the industrial partner Primetals(former Siemens VAI)

摘　　要：A volume average solidification model is extended to incorporate fragmentation as the source of equiaxed crystals during mixed columnar-equiaxed solidification. This study is to use this model to analyze the role of fragmentation in the formation of as-cast structure. Test simulations are made for the solidification of a model alloy(Sn-10wt.%Pb) with two different geometries. The first one is a 2D rectangular domain(50 × 60 mm^2) as cooled from the top boundary. Solidification starts unidirectionally as columnar structure from the top. The solute(Pb) enriched interdendritic melt is heavier than the bulk melt, and sinks downwards, hence leads to solutal convection. Fragmentation phenomenon occurs near the columnar tip front. The fragments are transported out of the columnar region, and they continue to grow and sink, and finally settle down and pile up at the bottom. The growing columnar structure from the top and pile-up of equiaxed crystals from the bottom finally lead to a mixed columnar-equiaxed structure, in turn leading to a columnar-to-equiaxed transition(CET). The second geometry is a 3D plate, 100 × 60 ×10 mm^3, as cooled laterally from one side. It was cast experimentally and analyzed for the as-cast structure. The equiaxed fragments are produced in the solidification front and transported into the bulk melt, leading to a special pattern of as-cast structure: columnar structure in the cool wall side and equiaxed structure in the upper left corner near the hot wall side, extending downwards to the middle bottom region. Numerically calculated as-cast structures agree with the experiment results.A volume average solidification model is extended to incorporate fragmentation as the source of equiaxed crystals during mixed columnar-equiaxed solidification. This study is to use this model to analyze the role of fragmentation in the formation of as-cast structure. Test simulations are made for the solidification of a model alloy（Sn-10wt.%Pb） with two different geometries. The first one is a 2D rectangular domain（50 × 60 mm^2） as cooled from the top boundary. Solidification starts unidirectionally as columnar structure from the top. The solute（Pb） enriched interdendritic melt is heavier than the bulk melt, and sinks downwards, hence leads to solutal convection. Fragmentation phenomenon occurs near the columnar tip front. The fragments are transported out of the columnar region, and they continue to grow and sink, and finally settle down and pile up at the bottom. The growing columnar structure from the top and pile-up of equiaxed crystals from the bottom finally lead to a mixed columnar-equiaxed structure, in turn leading to a columnar-to-equiaxed transition（CET）. The second geometry is a 3D plate, 100 × 60 ×10 mm^3, as cooled laterally from one side. It was cast experimentally and analyzed for the as-cast structure. The equiaxed fragments are produced in the solidification front and transported into the bulk melt, leading to a special pattern of as-cast structure： columnar structure in the cool wall side and equiaxed structure in the upper left corner near the hot wall side, extending downwards to the middle bottom region. Numerically calculated as-cast structures agree with the experiment results.

关 键 词：MACROSTRUCTURE interdendritic fluid flow FRAGMENTATION 

分 类 号：TP391.99[自动化与计算机技术—计算机应用技术]