MnE21镁合金轧制薄带的组织和性能  被引量:4

Microstructure and property of MnE21 magnesium alloy rolling sheet

在线阅读下载全文

作  者:张瑜 赵红阳[2] 胡小东[2] 房立强 

机构地区:[1]辽宁科技大学研究生院,辽宁鞍山114001 [2]辽宁科技大学材料与冶金学院,辽宁鞍山114001

出  处:《轻合金加工技术》2017年第12期18-24,共7页Light Alloy Fabrication Technology

摘  要:为了获得稀土镁合金薄带,采用挤压-轧制联合工艺路线,对厚度为1.4 mm的MnE21镁合金挤压板坯进行轧制试验。采用温轧工艺轧制出厚度为0.5 mm、0.4 mm、0.3 mm、0.2 mm的薄带,并对不同厚度的轧制薄带进行了微观组织和力学性能的对比分析。结果表明,不同厚度的薄带的抗拉强度Rm相差并不明显,Rm维持在200 N/mm2左右,但随着板带减薄,各向异性逐渐减小。MnE21镁合金薄带中的稀土相细小且均匀分布,合金的组织得到充分细化。In order to obtain thin sheets of magnesium alloy with rare earth, 1.4 mm extruded plates were warm rolled to 0.5 mm, 0.4 mm, 0.3 mm and 0.2 mm sheets at various reduction rates with the extrusion-rolling combined technology. Microstructure and mechanical properties of MnE21 sheets with different thicknesses were analyzed after rolling. The tensile strength is about 200 N/mm^2 with inconspicuous difference and the anisotropy decreases as the sheets become thinner. The fine rare earth phase is distributed homogenously in the rolling sheets and the grains are refined sufficiently.

关 键 词:MnE21镁合金 挤压 轧制 薄带 组织 性能 

分 类 号:TG339[金属学及工艺—金属压力加工]

 

参考文献:

正在载入数据...

 

二级参考文献:

正在载入数据...

 

耦合文献:

正在载入数据...

 

引证文献:

正在载入数据...

 

二级引证文献:

正在载入数据...

 

同被引文献:

正在载入数据...

 

相关期刊文献:

正在载入数据...

相关的主题
相关的作者对象
相关的机构对象