退火温度对5754铝合金冷轧板组织和性能的影响  

Effects of annealing temperatures on the microstructure and properties of 5754 Al-alloy cold rolling plate

作　　者：何建贤[1] 赵启忠[1] 朱希一 杨鸿驰 

机构地区：[1]广西南南铝加工有限公司,广西南宁530031

出　　处：《轻合金加工技术》2017年第12期29-31,41,共4页Light Alloy Fabrication Technology

摘　　要：选择冷变形率为50%、厚度为3.1mm的5754铝合金冷轧板,研究不同退火温度对冷轧板组织和性能的影响,以30℃间隔为每一个实验点,退火温度范围是从常温至600℃。实验研究结果显示,5754铝合金冷轧板在150℃已经进入回复阶段,组织中的晶粒并无明显变化,强度降低、塑性有所提升;当270℃退火时,组织已经发生再结晶;随着温度继续升高,当温度到达420℃时,晶粒略有长大;当温度升至600℃时,晶粒已异常长大。The research was conducted on the effects of different annealing temperatures （ every 30℃ from room temperature to 600℃） on the microstructure and properties of 3.1 mm thick cold rolling plates of 5754 aluminum alloy with cold deformation rate of 50%. The results show that the plate at 150℃ has entered the recovery stage, grains haven＇t changed greatly, strength is reduced and plasticity＂ is improved; recrystallization has occurred at 270℃; grains has grown up a little at 420℃; and grains have grown up exceptionally at 600℃.

关 键 词：5754铝合金冷轧板 组织 性能 退火 

分 类 号：TG146.21[一般工业技术—材料科学与工程] TG166.3[金属学及工艺—金属材料]