有机导电纤维混纺纱开发实践  

Development Practice of Organic Conductive Fiber Blended Yarn

作　　者：王显方[1] WANG Xian-fang(Shaanxi Polytechnic Institute, Xianyang 712000, Shannxi, China)

机构地区：[1]陕西工业职业技术学院,陕西咸阳712000

出　　处：《合成材料老化与应用》2017年第6期100-102,107,共4页Synthetic Materials Aging and Application

基　　金：陕西工业职业技术学院专项科研基金项目(ZK16-12)

摘　　要：为了生产导电纤维混纺纱,分析了导电纤维的性能,探讨26.4tex导电纤维、粘胶和涤纶混纺纱成纱工艺过程及纺纱工艺要点,结果表明:混纺纱成纱条干CV为16.48%,单纱断裂强力为13.65N/dtex,重量偏差为CV±2.0%,比电阻为1.2×10~6Ω·g/cm^2,其成纱各项性能指标较优,能满足抗静电织物用纱的需要,具有广阔的市场前景。In order to produce conductive fiber blended yarn,the properties of conductive fiber was analyzed,and the yarn process and spinning process for 26. 4 tex conductive fiber,viscose and polyester blended yarn was investigated. Reslt shows that blended yarn evenness CV is 16. 48%,single yarn breaking strength is 13. 65 N/dtex,the weight deviation is CV ± 2%,specific resistance is 1. 2 × 10~6Ω·g/cm^2,the yarn performance is good,can satisfy the antistatic fabric yarn.

关 键 词：导电纤维 混纺纱 工艺参数 开发 

分 类 号：TS104.2[轻工技术与工程—纺织工程]