耐贮存改性酚醛树脂交联剂的合成及性能评价  

Synthesis and Property Evaluation of Storable Modified Phenolic Resin Cross-Linking Agent

作　　者：张贵清 孙磊 夏烨 徐鸿志 郝志伟 

机构地区：[1]中国石油集团工程技术研究公司,天津300451

出　　处：《石油钻探技术》2017年第6期99-104,共6页Petroleum Drilling Techniques

摘　　要：目前国内油田剖面调整作业中常用的酚醛树脂交联剂贮存有效期短,无法满足长周期施工作业需求,为此,采用水杨酸类改性剂合成了改性酚醛树脂交联剂,并应用核磁共振氢谱表征了改性酚醛树脂的分子结构。通过室内试验考察了改性剂加量、催化剂加量及高温对改性酚醛树脂的贮存有效期及凝胶强度的影响,研究了交联剂加量、温度和矿化度对改性酚醛树脂交联体系成胶时间及凝胶强度的影响,评价了改性酚醛树脂交联体系的热稳定性能、封堵性能及提高采收率效果。试验结果表明,改性酚醛树脂分子上引入了具有空间位阻效应的酯基结构,其贮存有效期大幅延长,常温条件下贮存有效期达到234d,45℃恒温条件下贮存有效期大于90d;改性酚醛树脂交联体系在60~100℃及矿化度小于20 000mg/L条件下可生成高强度凝胶;改性酚醛树脂交联体系180d黏度保留率大于88%,封堵率大于98%,采收率可提高14.6百分点。研究表明,耐贮存改性酚醛树脂交联剂不仅具有良好的交联性能,还具有良好的耐贮存性能,满足长周期施工作业的需要,具有较好的应用前景。At present,phenolic resin cross-linking agents commonly used in profile control and flooding operations in domestic oilfields have short storage period which makes it unable to meet the requirements of long period field operations.Under such circumstances,the modified phenolic resin cross-linking agents were synthesized by using salicylic acid modifier.Molecular structures of modified phenolic resins were characterized by 1 H NMR,and researchers investigated the effects of modifier dosages,catalyst dosages and high temperatures on the storage life and gel strength of modified phenolic resin.The effects of cross-linking agent dosage,temperature and salinity on gelling time and gel strength of modified phenolic resin crosslinked system were also investigated.The thermal stability,plugging performances and EOR effects of the modified phenolic resin cross-linked system were assessed.Lab test results showed that the ester structure with steric hindrance that was introduced into the modified phenolic resin could prolong the storage life significantly,resulting in a storage life of modified phenolic resin up to 234 dat room temperature,and over90 dat 45 ℃.The cross-linked system can form strong gel at temperatures of 60-100 ℃ or salinities of no more than 20 000 mg/L.Studies showed that the viscosity retention rate of the cross-linked system in 180 days was more than 88%,and the plugging ratio more than 98%.In this case,the EOR increased by14.6%.The synthetically modified phenolic resin cross-linking agents not only have outstanding cross-linking properties,but also have excellent storage performances,so as to meet the demands of long-term operations,with excellent prospects for application.

关 键 词：改性酚醛树脂 剖面调整 贮存有效期 提高采收率 

分 类 号：TE39[石油与天然气工程—油气田开发工程]