废轮胎热解炭黑在天然橡胶中的应用研究  

Application of Pyrolytic Carbon Black from Waste Tires in Natural Rubber

作　　者：周作艳 夏琳[1] 王军晓[2] 朱永宁[2] 

机构地区：[1]青岛科技大学橡塑材料与工程教育部重点实验室,山东青岛266042 [2]苏州宝化炭黑有限公司,江苏苏州215000

出　　处：《橡胶工业》2018年第1期56-59,共4页China Rubber Industry

基　　金：国家自然科学基金资助项目(51303092)

摘　　要：研究废轮胎热解炭黑(CB_P)对天然橡胶(NR)胶料各项性能的影响,并与炭黑N220,N330,N660和N774进行对比。结果表明:CB_P聚集体粒径分布宽,灰分含量远高于普通炭黑;添加CB_P的NR胶料的拉伸强度和撕裂强度很高,100%和300%定伸应力很低,耐磨性能和耐屈挠疲劳性能较差。The effects of pyrolytic carbon black（CBP） from waste tires on the properties of natural rubber（NR） compounds were investigated and compared with other kinds of carbon black such as N220,N330,N660 and N774. The results showed that,the particle size distribution of CBP aggregate was wide, and the ash content of CBP was much higher than that of conventional carbon black. With the incorporation of CBP into NR compound,the tensile strength and tear strength of the vulcanizate were quite high,while the modulus at 100% and 300% elongation were low,the abrasion resistance and flexural fatigue resistance were inferior to those of the NR vulcanizates filled by conventional carbon black.

关 键 词：废轮胎 热解炭黑 天然橡胶 结构度 耐磨性能 耐屈挠疲劳性能 

分 类 号：TQ330.381[化学工程—橡胶工业] TQ332.6