船用5083铝合金厚板搅拌摩擦焊接工艺研究  

Study on Friction Stir Welding Process for Marine 5083 Aluminum Alloy Thick Plate

作　　者：李瑞武 杨青云[1] 邱胜闻 张明辉[1] 郭宇凡[1] LI Ruiwu;YANG Qingyun;QIU Shengwen;ZHANG Minghui;GUO Yufan(Luoyang Ship Material Research Institute, Luoyang 471023, China)

机构地区：[1]中国船舶重工集团公司第七二五研究所,河南洛阳471023

出　　处：《材料开发与应用》2017年第6期40-45,共6页Development and Application of Materials

摘　　要：研究了30 mm厚铝合金5083板材双面对接焊不同焊接速度和旋转速度的焊接参数组合对焊接接头成型质量及力学性能的影响,结果表明,当焊接参数处于旋转速度为400 r/min^600 r/min,焊接速度为80mm/min^120 mm/min的工艺参数窗口内时,可以获得焊缝成型质量与抗拉性能优异的焊缝。Effects of welding speed and rotational speed on the iormation and mecbamcal properties oI me welueu joint of zu mm- thick 5083 alluminum alloy by friction stir welding were studied. Results showed the forming quality and tensile property of weld can reach that of base metal when the optimum range of friction stir welding process parameter was obtained for 5083 aluminum alloy with thickness of 30mm. were excellent when the rotational speed was within 400 - 600 r/min and the welding speed 80 - 120 mm/min.

关 键 词：搅拌摩擦焊 铝合金 厚板 旋转速度 焊接速度 接头性能 

分 类 号：TG457.14[金属学及工艺—焊接]