Effect of Ca-Fe oxides additives on NOx reduction in iron ore sintering  

作　　者：Zhi-yuan Yu Xiao-hui Fan Min Gan Xu-ling Chen 

机构地区：[1]Hunan Research Academy of Environmental Sciences,Changsha 410004,Hunan,China [2]School of Mineral Processing and Bioengineering,Central South University,Changsha 410083,Hunan,China

出　　处：《Journal of Iron and Steel Research International》2017年第12期1184-1189,共6页

摘　　要：As the emission control regulations get stricter,the NO;reduction in the sintering process becomes an important environmental concern owing to its role in the formation of photochemical smog and acid rain.The NOxemissions from the sintering machine account for 48% of total amount from the iron and steel industry.Thus,it is essential to reduce NO;emissions from the sintering machine,for the achievement of clean production of sinter.Ca-Fe oxides,serving as the main binding phase in the sinter,are therefore used as additives into the sintering mixture to reduce NOxemissions.The results show that the NO;reduction ratio achieves 27.76% with 8% Ca-Fe oxides additives since the Ca-Fe oxides can advance the ignition and inhibit the nitrogen oxidation compared with the conventional condition.Meanwhile,the existence of Ca-Fe oxides was beneficial to the sinter quality since they were typical low melting point compounds.The optimal mass fraction of Ca-Fe oxides additives should be less than 8%since the permeability of sintering bed was significantly decreased with a further increase of the Ca-Fe oxides fines,inhibiting the mineralization reaction of sintering mixture.Additionally,the appropriate particle size can be obtained when mixing an equal amount of Ca-Fe oxides additives of-0.5 mm and 0.5-3.0 mm in size.As the emission control regulations get stricter,the NO_x reduction in the sintering process becomes an important environmental concern owing to its role in the formation of photochemical smog and acid rain.The NOxemissions from the sintering machine account for 48% of total amount from the iron and steel industry.Thus,it is essential to reduce NO_x emissions from the sintering machine,for the achievement of clean production of sinter.Ca-Fe oxides,serving as the main binding phase in the sinter,are therefore used as additives into the sintering mixture to reduce NOxemissions.The results show that the NO_x reduction ratio achieves 27.76% with 8% Ca-Fe oxides additives since the Ca-Fe oxides can advance the ignition and inhibit the nitrogen oxidation compared with the conventional condition.Meanwhile,the existence of Ca-Fe oxides was beneficial to the sinter quality since they were typical low melting point compounds.The optimal mass fraction of Ca-Fe oxides additives should be less than 8%since the permeability of sintering bed was significantly decreased with a further increase of the Ca-Fe oxides fines,inhibiting the mineralization reaction of sintering mixture.Additionally,the appropriate particle size can be obtained when mixing an equal amount of Ca-Fe oxides additives of-0.5 mm and 0.5-3.0 mm in size.

关 键 词：Iron ore sintering NOx reduction Ca-Fe oxide Coke combustion Sinter index 

分 类 号：TF046.4[冶金工程—冶金物理化学]