GCr15钢大方坯传热凝固数值模拟  被引量:7

Numerical simulation of heat transfer and solidification in GCr15 steel bloom

在线阅读下载全文

作  者:王德炯 焦帅[2] 殷皓 孙彦辉 赵勇 李晓滨[4] 

机构地区:[1]南京钢铁有限公司,江苏南京210035 [2]北京科技大学冶金与生态工程学院,北京100083 [3]北京科技大学钢铁共性技术协同创新中心,北京100083 [4]中冶建筑研究总院有限公司,北京100088

出  处:《炼钢》2018年第1期30-35,共6页Steelmaking

基  金:国家高技术研究发展计划(863计划)资助项目(2015AA03A502)

摘  要:以某钢厂GCr15钢大方坯为研究对象,采用ProCAST软件建立凝固数学模型,研究了过热度、拉速和比水量对大方坯凝固过程的影响,并通过对铸坯中心固相率及液芯长度的分析,确定了最佳末端电磁搅拌位置,并优化了拉速。研究结果表明:过热度对铸坯凝固影响最小,随着过热度增加,铸坯表面温度升高,铸坯液芯长度和液相区长度均随之增加,而两相区长度则随之减小;拉速对铸坯凝固影响最大,拉速提高,铸坯表面温度、液芯长度、两相区长度、液相区长度均增大;比水量增加,铸坯表面温度降低,液芯长度减小;当比水量为0.29 L/kg时,过热度应控制在15~35℃,拉速需控制在0.46~0.49m/min,且最佳拉速为0.48 m/min。The solidification mathematical model was established by using GCr15 steel bloom as a research object.The effects of superheat,casting speedand cooling water on the solidification process of bloom were studied.By analyzing the center solid fraction and liquid core length of the bloom,the optimum F-EMS position was determined and the casting speed was optimized.The results showed that the superheat had the little effect on the solidification of the bloom.With the increase of the superheat,the surface temperature of the billet increased,the length of liquid core and the length of liquid zone increasd,while the length of twophase zone decreased.The effect of casting speed was the largest,the surface temperature,the length of liquid core,the length of two-phase zone and the length of liquid zone were all increased with the increase of the casting speed.With the increase of the water ratio,the surface temperature of the billet and the length of the liquid core decreasd.When the water ratio was 0.29 L/kg,the superheat degree should be controlled at 15-35 ℃,the casting speed could be controlled in the range of 0.46-0.49 m/min,and the best casting speed was 0.48 m/min.

关 键 词:大方坯 数值模拟 中心固相率 液芯长度 

分 类 号:TF777.2[冶金工程—钢铁冶金]

 

参考文献:

正在载入数据...

 

二级参考文献:

正在载入数据...

 

耦合文献:

正在载入数据...

 

引证文献:

正在载入数据...

 

二级引证文献:

正在载入数据...

 

同被引文献:

正在载入数据...

 

相关期刊文献:

正在载入数据...

相关的主题
相关的作者对象
相关的机构对象