胶体晶体模板法制备有序多孔镁铝水滑石  

Preparation of Magnesium Aluminum Hydrotalcite with Orderly Porous Structure by Colloidal Crystal Template

作　　者：任秀梅[1] 周爱军[1] 孙贺雷 夏瑞 

机构地区：[1]武汉工程大学材料科学与工程学院,湖北武汉430205

出　　处：《武汉工程大学学报》2018年第1期52-56,共5页Journal of Wuhan Institute of Technology

基　　金：湖北省自然科学基金(2014CFB785)

摘　　要：以粒径约1μm的单分散三聚氰胺-甲醛微球制备得到胶体晶体模板,采用低过饱和沉淀法制备的镁铝摩尔比为2∶1的镁铝水滑石,将合成的水滑石悬浊液通过毛细效应的作用填充至胶体晶体模板间,待固化后经过煅烧去除胶体晶体模板,制备有序多孔镁铝水滑石。通过傅里叶红外光谱、X射线衍射分析、热重分析、差示扫描热分析、扫描电子显微镜对有序多孔镁铝水滑石的结构及形貌进行表征。结果表明,当加入体积分数为5%镁铝水滑石悬浊液时,去除模板后可得到孔径大小较为均一且排列有序的多孔镁铝水滑石。The colloidal crystal templates were prepared by using monodisperesed melamine formaldhydemicrospheres with particle sizes about 1 μm,and the Mg-Al hydrotalcite-like compounds with 2：1 mole ratio ofMg and Al were successfully synthesized by a supersaturated precipitation method. Then the magnesiumaluminum hydrotalcite serous was filled into the colloidal crystal templates with the effection of capillary,andthe colloidal crystal templates were removed by calcification after the solidification process. The morphology andstructure of orderly porous magnesium aluminum hydrotalcite were characterized by Fourier transform infraredspectroscopy,X-ray diffraction analysis,thermogravimetric analysis,differential scanning calorimeter andscanning electron microscopy. The results showed that the orderly porous magnesium aluminum hydrotalcitewith more uniform aperture size was obtained when the volume fraction of magnesium aluminum hydrotalciteserous was 5%.

关 键 词：有序多孔材料 镁铝水滑石 胶体晶体 模板法 三聚氰胺-甲醛微球 

分 类 号：TB303[一般工业技术—材料科学与工程]