球磨工艺对永磁铁氧体磁性能的影响  

Effect of ball milling process on magnetic properties of permanent ferrite

作　　者：张伟[1] 邱伟国[1] 赵修彬[1] 

机构地区：[1]中钢集团安徽天源科技股份有限公司

出　　处：《金属功能材料》2018年第1期30-32,共3页Metallic Functional Materials

摘　　要：对球磨工艺进行了优化,分别研究了球磨用钢球种类、材质、直径大小、球磨机转速以及球磨时间对永磁铁氧体磁性能和料浆粒度分布的影响,结果表明,使用轴承钢球球磨所得产品的磁性能（B_r,H_（cb）,H_（cj））明显好于合金钢球球磨所得产品的磁性能。选择ф6mm与ф4.8mm轴承钢球按照4∶6的比例配比,并将球磨机转速选定为22r/min,球磨10h,所获得的料浆磁性能最好,料浆粒度分布好。The ball milling process is optimized. The effects of ball type, material, diameter, speed of ball mill and ball milling time on the magnetic properties and particle size distribution of permanent ferrite were studied, The results show that the magnetic properties （Br, Hcb, Hcj） of the products obtained by ball milling with ball bearings are better than those obtained by ball milling of alloy steels. Choose 6 mm and 4.8 mm bearing steel ball according to the ratio of 4 to 6, and select the ball mill speed as 22 r/min, ball milling 10h, the obtained slurry has the best magnetic properties, and the slurry size distribution is good.

关 键 词：湿磨 轴承钢球 粒度分布 转速 

分 类 号：TM277[一般工业技术—材料科学与工程]