新型微弧氧化涂层镁-锌-钙合金支架/自体颗粒骨修复兔临界性骨缺损的研究  

In vivo study of a novel micro-arc oxidation coated magnesium-zinc-calcium alloy scaffold/autologous bone particles repairing critical size bone defect in rabbit

作　　者：张楠[1,2] 刘娜[1] 孙楚 朱剑峰[1] 王东旭[1] 戴云峰 吴云峰 王亚明[3] 李军雷 赵德伟[4] 闫景龙[2] ZHANG Nan;LIU Na;SUN Chu;ZHU Jianfeng;WANG Dongxu;DAI Yunfeng;WU Yunfeng;WANG Yaming;ZHAO Dewei;YAN Jinglong(Department of Orthopedics, Second Affiliated Hospital of Qiqihar Medical College, Qiqihar Heilongjiang, 161000, P.R.China;Department of Orthopedics, Second Affiliated Hospital of Harbin Medical University, Harbin Heilongjiang, 150086, P.R.China;Institute for Advanced Ceramics, Harbin Institute of Technology, Harbin Heilongjiang, 150001, P.R.China;Department of Orthopedics, Affiliated Zhongshan Hospital of Dalian University, Dalian Liaoning, 116001, P.R. China)

机构地区：[1]齐齐哈尔医学院附属第二医院骨科,黑龙江齐齐哈尔161000 [2]哈尔滨医科大学附属第二医院骨科,哈尔滨150086 [3]哈尔滨工业大学材料学院,哈尔滨150001 [4]大连大学附属中山医院骨科,辽宁大连116001

出　　处：《中国修复重建外科杂志》2018年第3期298-305,共8页Chinese Journal of Reparative and Reconstructive Surgery

基　　金：齐齐哈尔医学院临床科研基金项目(QY2015L-05;QY2015L-07)~~

摘　　要：目的探讨一种新型微弧氧化(micro-arc oxidation,MAO)涂层镁(Mg)-锌(Zn)-钙(Ca)合金支架/自体颗粒骨修复兔临界性骨缺损(critical size bone defect,CSD)的效果,以及该支架在体内的耐腐蚀性和生物相容性。方法将72只新西兰白兔随机分为3组(n=24),A组为无涂层Mg-Zn-Ca合金支架组;B组为10μm厚MAO涂层Mg-Zn-Ca合金支架组;C组为单纯自体颗粒骨植骨组。所有动物制备双侧尺骨15 mm长CSD模型,A、B组将截取的尺骨制成颗粒骨后填充至支架内修复尺骨缺损,C组采用自体颗粒骨修复。术后2、4、8、12周,行大体观察并记录局部皮下积气量;X线片和Van Gieson染色观察骨缺损愈合情况,根据Lane-Sandhu标准行X线片评分;Micro-CT扫描观察并计算支架降解丢失体积百分比(ΔV)及降解速度(corrosion rate,CR);监测实验过程中血清Mg^(2+)、Ca^(2+)浓度变化,并于术后12周收集肝、脑、肾和脾组织行病理学观察。结果术后2、4、8周B组皮下积气量少于A组,其中2、4周两组间比较差异有统计学意义(P<0.05);但术后12周时B组显著多于A组(P<0.05)。术后4、8周C组X线片评分显著高于A、B组(P<0.05),术后8周时B组显著高于A组(P<0.05);术后12周B、C组显著高于A组(P<0.05),但B、C组间差异无统计学意义(P>0.05),同时B组骨缺损部位新骨塑形明显优于A组。Micro-CT示术后4、8周,B组CR及ΔV均显著低于A组(P<0.05)。Van Gieson染色示B组较A组具有更好的生物相容性和促成骨性;血清离子监测结果显示术后各时间点3组血清Mg^(2+)、Ca^(2+)浓度比较,差异均无统计学意义(P>0.05);术后12周,3组实验动物肝、脑、肾及脾组织HE染色均未见明显病理改变。结论新型MAO涂层Mg-Zn-Ca合金支架/自体颗粒骨能够有效修复CSD;同时,10μm厚MAO涂层能有效改良Mg-Zn-Ca合金支架的骨修复效果、耐腐蚀性及生物相容性。Objective To evaluate the effect of a novel micro-arc oxidation（MAO） coated magnesium-zinccalcium（Mg-Zn-Ca） alloy scaffold/autologous bone particles to repair critical size bone defect（CSD） in rabbit and explore the novel scaffold in vivo corrosion resistance and biocompatibility. Methods Seventy-two New Zealand white rabbits were randomly divided into 3 groups（n=24）, group A was uncoated Mg-Zn-Ca alloy scaffold group, group B was 10 μm MAO coated Mg-Zn-Ca alloy scaffold group, and group C was control group with only autologous bone graft. The animals were operated to obtain bilateral ulnar CSD（15 mm in length） models. The bone fragment was removed and minced into small particles and were filled into the scaffolds of groups A and B. Then, the scaffolds or autologous bone particles were replanted into the defects. The animals were sacrificed at 2, 4, 8, and 12 weeks after surgery（6 rabbits each group）. The local subcutaneous pneumatosis was observed and recorded. The ulna defect healing was evaluated by X-ray image and Van Gieson staining. The X-ray images were assessed and scored by Lane-Sandhu criteria. The percentage of the lost volume of the scaffold（ΔV） and corrosion rate（CR） were calculated by the Micro-CT. The Mg^（2＋） and Ca^（2＋） concentrations were monitored during experiment and the rabbit liver, brain, kidney, and spleen were obtained to process HE staining at 12 weeks after surgery. Results The local subcutaneous pneumatosis in group B was less than that in group A at 2, 4, and8 weeks after surgery, showing significant differences between 2 groups at 2 and 4 weeks after surgery（P〈0.05）; and the local subcutaneous pneumatosis was significantly higher in group B than that in group A at 12 weeks after surgery（P〈0.05）. The X-ray result showed that the score of group C was significantly higher than those of groups A and B at 4 and 8 weeks after surgery（P〈0.05）, and the score of group B was significantly higher than that of group A at 8 weeks（P

关 键 词：镁合金支架 临界性骨缺损 微弧氧化 耐腐蚀性 生物相容性 兔 

分 类 号：R318.08[医药卫生—生物医学工程] R68[医药卫生—基础医学]