Effect of Magnesium on the C-S-H Nanostructure Evolution and Aluminate Phases Transition in Cement-Slag Blend  

作　　者：丁庆军 YANG Jun 张高展 HOU Dongshuai 

机构地区：[1]School of Materials Science and Engineering, Wuhan University of Technology [2]Advanced Building Materials Key Laboratory of Anhui Province, Anhui Jianzhu University [3]Department of Civil Engineering, Qingdao Technological University

出　　处：《Journal of Wuhan University of Technology(Materials Science)》2018年第1期108-116,共9页武汉理工大学学报（材料科学英文版）

基　　金：Funded by National Natural Science Foundation of China(Nos.51778513,51402003,51578004);China Ministry of Science and Technology(No.2015CB655101)

摘　　要：The microstructural study was conducted on cement and cement-slag pastes immersed in different concentrations of Mg（NO3）2 solutions utilizing ^29Si, ^27Al NMR spectroscopy and XRD techniques. The results show that the hydration of both the cement and cement-slag pastes is delayed when the pastes are cured in Mg（NO3）2 solutions as compared to the pastes cured in water. Moreover, Mg^2＋ ions also exhibit an decalcifying and dealuminizing effect on the C-A-S-H in cement and cement-slag pastes, and thereby decrease Ca/Si and Al[4]/Si ratios of the C-A-S-H. The dealuminization of C-A-S-H is mitigated for cement-slag paste as compared to pure cement paste. The depolymerized calcium and aluminum ions from C-A-S-H gel mainly enter the pore solution to maintain the pH value and form Al^[6] in TAH, respectively. On the other hand, Mg^2＋ ions exert an impact on the intra-transition between Al^[6] species, from AFm and hydrogarnet to hydrotalcite-like phase. NO3^-ions are interstratified in the layered Mg-Al structure and formed nitrated hydrotalcite-like phase（Mg1-xAlx（OH）2（NO3）x·nH2O）. Results from both ^27Al NMR and XRD data show that ettringite seems not to react with Mg^2＋ ions.The microstructural study was conducted on cement and cement-slag pastes immersed in different concentrations of Mg（NO3）2 solutions utilizing ^29Si, ^27Al NMR spectroscopy and XRD techniques. The results show that the hydration of both the cement and cement-slag pastes is delayed when the pastes are cured in Mg（NO3）2 solutions as compared to the pastes cured in water. Moreover, Mg^2＋ ions also exhibit an decalcifying and dealuminizing effect on the C-A-S-H in cement and cement-slag pastes, and thereby decrease Ca/Si and Al[4]/Si ratios of the C-A-S-H. The dealuminization of C-A-S-H is mitigated for cement-slag paste as compared to pure cement paste. The depolymerized calcium and aluminum ions from C-A-S-H gel mainly enter the pore solution to maintain the pH value and form Al^[6] in TAH, respectively. On the other hand, Mg^2＋ ions exert an impact on the intra-transition between Al^[6] species, from AFm and hydrogarnet to hydrotalcite-like phase. NO3^-ions are interstratified in the layered Mg-Al structure and formed nitrated hydrotalcite-like phase（Mg1-xAlx（OH）2（NO3）x·nH2O）. Results from both ^27Al NMR and XRD data show that ettringite seems not to react with Mg^2＋ ions.

关 键 词：^29Si and ^27Al NMR magnesium ion C-A-S-H microstructure aluminate phases transition hydration slag incorporation 

分 类 号：TQ172.1[化学工程—水泥工业]