Enhanced sulfide chemisorption by conductive AI-doped ZnO decorated carbon nanoflakes for advanced Li-S batteries  

作　　者：Yangbo Kong Jianmin Luo Chengbin Jin Huadong Yuan Ouwei Sheng Liyuan Zhang Cong Fang Wenkui Zhang Hui Huang Yang Xia Chu Liang Jun Zhang Yongping Gan Xinyong Tao 

机构地区：[1]College of Materials Science and Engineering, Zhejiang University of Technology, Hangzhou 310014, China

出　　处：《Nano Research》2018年第1期477-489,共13页纳米研究（英文版）

摘　　要：Lithium-sulfur batteries have attracted significant attention recently due to their high theoretical capacity, energy density and cost effectiveness. However, sulfur cathodes suffer from issues such as shuttle effects, uncontrollable deposition of lithium sulfides species, and volume expansion of sulfur, which result in rapid capacity fading and low Coulombic efficiency. In recent years, metal-oxide nanostructures have been widely used in Li-S batteries, owing to their effective inhibition of the shuttle effect and controlled deposition of lithium sulfide. However, the nonconductive metal-oxides used in Li-S batteries suffer from extra diffusion process, which slows down the electrochemical reaction kinetics. Herein, we report the synthesis of carbon nanoflakes decorated with conductive aluminium-doped zinc oxide （AZO@C） nanoparticles, through a facile biotem- plating method using kapok fibers as both the template and carbon source. A sulfur cathode based on the AZO@C nanocomposites shows better electrochemical performance than those of cathodes based on ZnO and A1203 with poor conductivity, with a stable capacity of 927 mAh.g-1 at 0.1C （1C = 1,675 mA.g-1） after 100 cycles. A reversible capacity of 544 mAh.g-1 after 300 cycles was obtained even after increasing the current density to 0.5C, with a 0.039% capacity decay per cycle under a sulfur loading of 3.3 mg-cm-2. Moreover, a capacity of 466 mAh.g-1 after 100 cycles at 0.5C could still be obtained when the sulfur loading was increased to 6.96 mg.cm-2. The excellent electrochemical performance of the AZO@C/S composite can be attributed to its high conductivity of the polar AZO host, which suppresses the shuttle effect while simultaneously improving the redox kinetics in the reciprocal transformation of lithium sulfide species.Lithium-sulfur batteries have attracted significant attention recently due to their high theoretical capacity, energy density and cost effectiveness. However, sulfur cathodes suffer from issues such as shuttle effects, uncontrollable deposition of lithium sulfides species, and volume expansion of sulfur, which result in rapid capacity fading and low Coulombic efficiency. In recent years, metal-oxide nanostructures have been widely used in Li-S batteries, owing to their effective inhibition of the shuttle effect and controlled deposition of lithium sulfide. However, the nonconductive metal-oxides used in Li-S batteries suffer from extra diffusion process, which slows down the electrochemical reaction kinetics. Herein, we report the synthesis of carbon nanoflakes decorated with conductive aluminium-doped zinc oxide （AZO@C） nanoparticles, through a facile biotem- plating method using kapok fibers as both the template and carbon source. A sulfur cathode based on the AZO@C nanocomposites shows better electrochemical performance than those of cathodes based on ZnO and A1203 with poor conductivity, with a stable capacity of 927 mAh.g-1 at 0.1C （1C = 1,675 mA.g-1） after 100 cycles. A reversible capacity of 544 mAh.g-1 after 300 cycles was obtained even after increasing the current density to 0.5C, with a 0.039% capacity decay per cycle under a sulfur loading of 3.3 mg-cm-2. Moreover, a capacity of 466 mAh.g-1 after 100 cycles at 0.5C could still be obtained when the sulfur loading was increased to 6.96 mg.cm-2. The excellent electrochemical performance of the AZO@C/S composite can be attributed to its high conductivity of the polar AZO host, which suppresses the shuttle effect while simultaneously improving the redox kinetics in the reciprocal transformation of lithium sulfide species.

关 键 词：lithium-sulfur battery aluminium-doped zincoxide CONDUCTIVE nanostructure BIOTEMPLATE carbon nanoflakes 

分 类 号：O625.463[理学—有机化学] X832.02[理学—化学]