1000m^3高炉炉缸炉底破损原因分析  

Damage Survey and Corrosion Mechanisation on Hearth Bottom of 1 000 m^3 Blast Furnace

作　　者：李小静[1] 李帮平[1] 张晓萍[1] 宋灿阳[1] Li Xiaojing, Li Bangping, Zhang Xiaoping ,Song Canyang(Maanshan Iron ＆ Steel Co. , Ltd)

机构地区：[1]马鞍山钢铁股份有限公司

出　　处：《安徽冶金》2018年第1期29-33,共5页Anhui Metallurgy

摘　　要：1 000m^3高炉炉缸下部及底部呈"圆锅底"型侵蚀,实际炉缸直径变大,炉底加深。缸炉底炭砖破坏的主要原因是K_2O、Na_2O和Zn的化学性侵蚀和铁水的浸入式侵蚀。为减缓炉缸和炉底炭砖侵蚀,建议改善显气孔率、抗碱侵蚀能力和抗铁水溶蚀性。The hearth bottom of 1000 m3 blast furnace iscorroded as a round pot. The actual diameter of thehearth gets larger and the bottom of the furnace s deepened. All these are caused by chemcal erosion with K2O, Na2O, zinc, and hot metal immersion. In order to release he erosion of hearth and bottom brick, It is suggested to improve the apparent porosity, alkali erosion resistance and corrosion resistance of hot metal.

关 键 词：1000m3高炉 炉缸炉底 破损调查 侵蚀机理 