Self-polymerization and co-polymerization kinetics of gadolinium methacrylate  

作　　者：Chunhong Wang Shuai Wang Yujuan Zhang Zhifeng Wang Junliang Liu Ming Zhang 

机构地区：[1]School of Chemistry and Chemical Engineering,Yangzhou University [2]Testing Center,Yangzhou University

出　　处：《Journal of Rare Earths》2018年第3期298-303,共6页稀土学报（英文版）

基　　金：Project supported by Graduate Student Research Innovation Project(KYLX_1337)

摘　　要：Gadolinium methacrylate（Gd（MAA）3） was synthesized by using gadolinium oxide and methacrylic acid as the starting materials and its self-polymerization kinetic was studied based on non-isothermal and isothermal analysis. Moreover, the monomer reactivity ratios of methyl methacrylate（MMA） and Gd（MAA）3 were evaluated by using Kelen-Tiidos method. The thermal neutron shielding properties of PMMA and poly（MMA-co-Gd（MAA）3） were calculated by MCNP program. The results show that the selfpolymerization of Gd（MAA）3 can be initiated by thermal and free radical and its activation energy is103.35 kJ/mol or 58.55 kJ/mol correspondingly in the solid state or aqueous solution. The polymerization rate,Rp,under low conversion at 65 ℃ is expressed as Rp = K[M]^（1.05）[I]^（0.60）. The reactivity ratios of r1（MMA） and r2（Gd（MAA）3） are 0.225 and 1.340, respectively. The ability of thermal neutron shielding of poly（MMA-co-Gd（MAA）3） is increased by gadolinium contents and is far better than PMMA.Gadolinium methacrylate（Gd（MAA）3） was synthesized by using gadolinium oxide and methacrylic acid as the starting materials and its self-polymerization kinetic was studied based on non-isothermal and isothermal analysis. Moreover, the monomer reactivity ratios of methyl methacrylate（MMA） and Gd（MAA）3 were evaluated by using Kelen-Tiidos method. The thermal neutron shielding properties of PMMA and poly（MMA-co-Gd（MAA）3） were calculated by MCNP program. The results show that the selfpolymerization of Gd（MAA）3 can be initiated by thermal and free radical and its activation energy is103.35 kJ/mol or 58.55 kJ/mol correspondingly in the solid state or aqueous solution. The polymerization rate,Rp,under low conversion at 65 ℃ is expressed as Rp = K[M]^（1.05）[I]^（0.60）. The reactivity ratios of r1（MMA） and r2（Gd（MAA）3） are 0.225 and 1.340, respectively. The ability of thermal neutron shielding of poly（MMA-co-Gd（MAA）3） is increased by gadolinium contents and is far better than PMMA.

关 键 词：Gadolinium methacrylate Thermal analysis Polymerization kinetic Thermal neutron shielding Rare earths 

分 类 号：O634[理学—高分子化学]