High-temperature deformation behavior of a beta Ti-3.0Al-3.5Cr-2.0Fe-0.1B alloy  

作　　者：Wen-Tao Qu Xu-Guang Sun Song-Xiao Hui Zhen-Guo Wang Yan Li 

机构地区：[1]School of Mechanical Engineering,Xi'an Shiyou University [2]State Key Laboratory of Nonferrous Metals and Processes,General Research Institute for Nonferrous Metals [3]School of Materials Science and Engineering,Beihang University

出　　处：《Rare Metals》2018年第3期217-224,共8页稀有金属（英文版）

基　　金：financially supported by the.National Natural Science Foundation of China (No.51401027);the China Postdoctoral Science Foundation Funded Project (No.2016M591040)

摘　　要：The high-temperature deformation behavior of a beta Ti-3.0 Al-3.5 Cr-2.0 Fe-0.1 B alloy was investigated by a Gleeble-1500 D thermal simulator. The height reduction was 50%, corresponding to a true strain of 0.693. The strain rate ranging from 0.01 to 10.00 s^-1 and the deformation temperature ranging from 800 to 950 ℃ were considered.The flow stress and the apparent activation energy for deformation, along with the constitutive equation, were used to analyze the behavior of the Ti-3.0 Al-3.5 Cr-2.0 Fe-0.1 B alloy. The processing map was established. The effect of strain rate on the microstructure at 850 ℃ was evaluated.The flow stress-strain curves indicated that the peak flow stresses increased along with an increase in the strain rate and decreased as the deformation temperature increased.Based on the true stress-true strain curves, the constitutive equation was established and followed as the ε= 6.58×10-（10）[sinh（0.0113σ）]-（3.44）exp（-245481.3/RT）. The processing map exhibited the ＂unsafe＂ region at the strain rate of10 s^-1 and the temperature of 850 ℃,and the rest region was ＂safe＂. The deformation microstructure demonstrated that both dynamic recovery（DRV） and dynamic recrystallization（DRX） existed during deformation. At the lower strain rate of 0.01 s^-1, the main deformation mechanism was the DRV, and the DRX was the dominant deformation mechanism at the higher strain rate of 1.00 s^-1.The high-temperature deformation behavior of a beta Ti-3.0 Al-3.5 Cr-2.0 Fe-0.1 B alloy was investigated by a Gleeble-1500 D thermal simulator. The height reduction was 50%, corresponding to a true strain of 0.693. The strain rate ranging from 0.01 to 10.00 s^-1 and the deformation temperature ranging from 800 to 950 ℃ were considered.The flow stress and the apparent activation energy for deformation, along with the constitutive equation, were used to analyze the behavior of the Ti-3.0 Al-3.5 Cr-2.0 Fe-0.1 B alloy. The processing map was established. The effect of strain rate on the microstructure at 850 ℃ was evaluated.The flow stress-strain curves indicated that the peak flow stresses increased along with an increase in the strain rate and decreased as the deformation temperature increased.Based on the true stress-true strain curves, the constitutive equation was established and followed as the ε= 6.58×10-（10）[sinh（0.0113σ）]-（3.44）exp（-245481.3/RT）. The processing map exhibited the ＂unsafe＂ region at the strain rate of10 s^-1 and the temperature of 850 ℃,and the rest region was ＂safe＂. The deformation microstructure demonstrated that both dynamic recovery（DRV） and dynamic recrystallization（DRX） existed during deformation. At the lower strain rate of 0.01 s^-1, the main deformation mechanism was the DRV, and the DRX was the dominant deformation mechanism at the higher strain rate of 1.00 s^-1.

关 键 词：Titanium alloy Hot deformation Constitutive equation Processing map Microstructure 

分 类 号：TG146.23[一般工业技术—材料科学与工程]