Modeling reoxidation behavior of Al-Ti-containing steels by CaO-Al2O3-MgO-SiO2 slag  

作　　者：Ying Ren Li-feng Zhang Ying Zhang 

机构地区：[1]School of Metallurgical and Ecological Engineering,University of Science and Technology Beijing,Beijing 100083, China

出　　处：《Journal of Iron and Steel Research International》2018年第2期146-156,共11页

摘　　要：A kinetic model was developed using FactSage Macro Processing to simulate the reoxidation of Al-Ti-containing steels by CaO-Al2O3-SiO2-MgO slags. The calculated results show a good agreement with the experimental data. Thus, the developed kinetic model can be used to predict changes in slag, steel, and inclusion compositions during the reaction process. During the slag reoxidation process, the reactions occurring at slag-steel interface and in the bulk steel were confirmed to be the reduction of SiO2 by [All and [Til and the self-dissociation of SiO2 into [Si] and [O]. Increasing the ratio of CaO to SiO2 in the slag can significantly suppress the self-dissociation of SiO2 in the slag and lower the amount of inclusions produced during reoxidation. The formed inclusions changed from solid Al2O3 to Al2O3-TiOx inclusions, which was mainly dependent on the w（[Al]） and w（[Ti]）. The amount of inclusions was obviously influenced by the composition of the top slag.A kinetic model was developed using FactSage Macro Processing to simulate the reoxidation of Al-Ti-containing steels by CaO-Al2O3-SiO2-MgO slags. The calculated results show a good agreement with the experimental data. Thus, the developed kinetic model can be used to predict changes in slag, steel, and inclusion compositions during the reaction process. During the slag reoxidation process, the reactions occurring at slag-steel interface and in the bulk steel were confirmed to be the reduction of SiO2 by [All and [Til and the self-dissociation of SiO2 into [Si] and [O]. Increasing the ratio of CaO to SiO2 in the slag can significantly suppress the self-dissociation of SiO2 in the slag and lower the amount of inclusions produced during reoxidation. The formed inclusions changed from solid Al2O3 to Al2O3-TiOx inclusions, which was mainly dependent on the w（[Al]） and w（[Ti]）. The amount of inclusions was obviously influenced by the composition of the top slag.

关 键 词：Kinetic model SLAG INCLUSION REOXIDATION Al-Ti-containing steel 

分 类 号：TQ03[化学工程] TB332[一般工业技术—材料科学与工程]