Sintering characteristics and microwave dielectric properties of 0.5Ca_(0.6)La_(0.267)TiO_3-0.5Ca(Mg_(1/3)Nb_(2/3))O_3 ceramics prepared by reaction-sintering process  

作　　者：Jiamao Li Peng Xu Tai Qiu Lichun Yao 

机构地区：[1]School of Materials Science and Engineering,Anhui University of Technology [2]Jiangsu Collaborative Innovation Center for Advanced Inorganic Function Composites, Nanjing Tech University [3]College of Materials Science and Engineering,Nanjing Tech University

出　　处：《Journal of Rare Earths》2018年第4期404-408,共5页稀土学报（英文版）

基　　金：Project supported by Anhui Provincial Natural Science Foundation(1608085ME92)

摘　　要：0.5 Ca（0.6La0.267TiO3-0.5 Ca（Mg1/3Nb2/3）O3（5 CLT-5 CMN） ceramics were prepared by a reaction-sintering process and their sintering characteristics, microwave dielectric properties were investigated in detail.Without any calcination stage involved,a mixture of CaCO_3, La_2 O_3, TiO_2, MgO and Nb_2 O_5 was pressed and sintered directly. Pure phase 5 CLT-5 CMN ceramics with high density and dense microstructure can be obtained after sintered at 1400 ℃ for 4 h. Compared with those prepared by the conventional ceramic route, 5 CLT-5 CMN ceramics produced by the reaction-sintering process exhibit slightly higher dielectric constant and Q×f value. Fine microwave dielectric properties of ε_r= 56.4, Q×f= 48,550 GHz and T_f = ＋8.7 ppm/℃ for 5 CLT-5 CMN ceramics sintered at 1400 ℃ for 4 h are obtained, suggesting reactionsintering process is a simple and efficient method to produce pure phase 5 CLT-5 CMN ceramics as a potential candidate for the fabrication of microwave devices.0.5 Ca（0.6La0.267TiO3-0.5 Ca（Mg1/3Nb2/3）O3（5 CLT-5 CMN） ceramics were prepared by a reaction-sintering process and their sintering characteristics, microwave dielectric properties were investigated in detail.Without any calcination stage involved,a mixture of CaCO_3, La_2 O_3, TiO_2, MgO and Nb_2 O_5 was pressed and sintered directly. Pure phase 5 CLT-5 CMN ceramics with high density and dense microstructure can be obtained after sintered at 1400 ℃ for 4 h. Compared with those prepared by the conventional ceramic route, 5 CLT-5 CMN ceramics produced by the reaction-sintering process exhibit slightly higher dielectric constant and Q×f value. Fine microwave dielectric properties of ε_r= 56.4, Q×f= 48,550 GHz and T_f = ＋8.7 ppm/℃ for 5 CLT-5 CMN ceramics sintered at 1400 ℃ for 4 h are obtained, suggesting reactionsintering process is a simple and efficient method to produce pure phase 5 CLT-5 CMN ceramics as a potential candidate for the fabrication of microwave devices.

关 键 词：Microwave ceramics Sintering behavior Dielectric properties Reaction sintering Rare earths 