聚3,4-乙烯二氧噻吩在海洋微生物燃料电池阳极改性中的应用  

Application of Poly 3,4-ethylenedioxythiophene in Anode Modification of Marine Microbial Fuel Cells

作　　者：陈占飞 郑智 宋宇宁 刘红豆 王珊 徐方成[1] CHEN Zhanfei;ZHENG Zhi;SONG Yuning;LIU Hongdou;WANG Shan;XU Fangcheng(Collcgc of Chcmistry and Chcmical I＇2nginccring,Xiamcn Univcrsity,Xiamcn 361005,China)

机构地区：[1]厦门大学化学化工学院,福建厦门361005

出　　处：《厦门大学学报（自然科学版）》2018年第3期323-328,共6页Journal of Xiamen University：Natural Science

基　　金：国家自然科学基金(21273181);中国大洋重点项目(DY135-B-04,DY125-15-T-08);海洋地质国家重点实验室开放基金(MGK1207);清华大学环境模拟与污染控制国家重点实验室开放基金(11K08ESPCT)

摘　　要：采用聚3,4-乙烯二氧噻吩(PEDOT)修饰石墨阳极,采用恒电位仪、扫描电子显微镜、能谱仪对其进行表征,并探讨其在U型微生物燃料电池(MFC)中影响海洋产电菌Shewanella sp.S2产电的机制.结果表明:电化学法合成的PEDOT呈片状覆盖在石墨表面,并带有一些颗粒状凸起(直径约200nm).PEDOT修饰后,MFC表观内阻从471Ω下降到390Ω;稳定期的电流密度(173.6mA/m^2)是未修饰MFC(74.4mA/m^2)的2.33倍.扫描电镜结果显示,PEDOT修饰显著提高了产电菌在阳极表面的吸附量.由于电极表面的粗糙度远小于细菌尺寸,推测MFC产电能力的提高主要是由于PEDOT与产电菌间的电荷相互作用而不是电极表面粗糙度.In this study,poly （3,4- Cthylenedioxythiophene） （PEDOT） was used to modify the graphite anode.The modified graphite anode was characterized with Potcntiostat,scanning electron microscope （SEM）, energy disperse Spcctroscopy（EI）S） and its effects on current generation of U shaped microbial fuel cells （MFCs） were evaluated.The results showed that PEDOT was electrochemical ly Polymcrizcd and covered mainly in a sheet like form with 200 nm size dots on the anode surface. Polarization tests of the MFCs showed that,compared with the unmodified anode,apparent internal resistance declined from 471 t2 to 390 t2.Consequently,thc cur rent density at the plateau stage was enhanced greatly （by 2.33 times）, i.e., 173.6 mA/m2 for PEDOT modified type vs. 74.4 mA/m2 for the unmodified typc.SEM analysis showed that there were more SheuaneHa Sp. S2 cells adsorbed on the anode surface of the PEDOT modified type than that of the unmodified tyPc.Thc overall results confirmed that it was mainly the charge interaction between PEDOT and cxoclcctrogcns rather than the roughness improving marine MFC current production, because the roughness of both modified and unmodified anodes were much smaller than the size of S2 cells.

关 键 词：聚3 4-乙烯二氧噻吩 微生物燃料电池 Shewanellasp.S2 海洋产电菌 导电聚合物 