Energy transfer and 2 μm emission in Tm^(3+)/Ho^(3+) co-doped(Y_(0.87)La_(0.1)Zr_(0.03))_2O_3 nanopowders  

作　　者：Yaqian Chen Huanping Wang Xiaoting Zhang Zhen Xiao Qinghua Yang Ruoshan Lei Degang Deng Lihui Huang Shiqing Xu Yaqian Chen;Huanping Wang;Xiaoting Zhang;Zhen Xiao;Qinghua Yang;Ruoshan Lei;Degang Deng;Lihui Huang;Shiqing Xu(College of Materials Science and Engineering, China Jiliang University)

机构地区：College of Materials Science and Engineering, China Jiliang University, Hangzhou 310018, China

出　　处：《Journal of Rare Earths》2018年第5期468-473,共6页稀土学报（英文版）

基　　金：Project supported by Zhejiang Provincial Natural Science Foundation of China(LZ14B010001)

摘　　要：（Y0.87La0.1Zr0.03）2O3 nanopowders doped with various concentrations of Tm^3＋ and Ho^3＋ were prepared by the citrate method. The standard cubic Y2O3 phase can be matched in the Tm^3＋/Ho^3＋ co-doped（Y0.87La0.1Zr0.03）2 O3 nanopowders. The nanopowders exhibit average particle sizes of 40,60, 80 and 100 nm after calcinated at 900,1000,1100 and 1200℃,respectively. The energy transfer from Tm^3＋ to Ho^3＋ and the optimum fluorescence emission around 2 μm were investigated. Results indicate that the emission bands at around 1.86 and 1.95 μm correspond to 3 F4→3 H6 transition of Tm^3＋ and 5 I7→5 I8 transition of Ho^3＋, respectively.Better spectral properties were achieved in Tm^3＋/Ho^3＋ co-doped（Y0.87La0.1Zr0.03）2O3 nanopowders with the average size of 100 nm obtained at the conditions of the treatment of precursors calcinated at 1200 ℃ for 2 h doped with 1.5 mol% Tm^3＋ and 1 mol% Ho^3＋.（Y0.87La0.1Zr0.03）2O3 nanopowders doped with various concentrations of Tm^3＋ and Ho^3＋ were prepared by the citrate method. The standard cubic Y2O3 phase can be matched in the Tm^3＋/Ho^3＋ co-doped（Y0.87La0.1Zr0.03）2 O3 nanopowders. The nanopowders exhibit average particle sizes of 40,60, 80 and 100 nm after calcinated at 900,1000,1100 and 1200℃,respectively. The energy transfer from Tm^3＋ to Ho^3＋ and the optimum fluorescence emission around 2 μm were investigated. Results indicate that the emission bands at around 1.86 and 1.95 μm correspond to 3 F4→3 H6 transition of Tm^3＋ and 5 I7→5 I8 transition of Ho^3＋, respectively.Better spectral properties were achieved in Tm^3＋/Ho^3＋ co-doped（Y0.87La0.1Zr0.03）2O3 nanopowders with the average size of 100 nm obtained at the conditions of the treatment of precursors calcinated at 1200 ℃ for 2 h doped with 1.5 mol% Tm^3＋ and 1 mol% Ho^3＋.

关 键 词：Emission spectral Tm^3＋/Ho^3＋ Y2O3 La2O3-ZrO2 NANOPOWDERS Rare earths 

分 类 号：TB383[一般工业技术—材料科学与工程]