硅烷偶联剂改性彩色沥青混合料的路用性能  

Pavement Performance of Colored Asphalt Concrete Modified With Silane Coupling Agent

作　　者：杨月青 唐新德[1] 谭旭翔[1] 胡秀颖[1] 薛俊磊 郭斌 YANG Yue-qing;TANG Xin-de;TAN Xu-xiang;HU Xiu-ying;XUE Jun-lei;GUO Bin(Traffic Materials Study Center, Shandong Jiaotong University, Jinan 250357, Chin)

机构地区：[1]山东交通学院交通材料研究中心

出　　处：《公路》2018年第7期91-94,共4页Highway

基　　金：山东省科技发展计划项目,项目编号2014GGX102013

摘　　要：利用硅烷偶联剂对彩色沥青混凝土集料进行表面改性,以提高彩色沥青胶结料与集料的相容性,增强彩色沥青混合料的路用性能并揭示其增强机理。硅烷偶联剂通过水解反应形成硅醇,然后与集料表面的羟基作用形成偶联层,有效提高了彩色沥青胶结料与石料的界面作用力。马歇尔试验、浸水马歇尔试验、车辙试验和低温弯曲试验结果表明,经硅烷偶联剂改性的彩色沥青混合料具有良好的水稳性和高低温性能。To improve the compatibility of colored asphalt cement and concrete aggregates, silanecoupling agent is employed for the surface modification of concrete aggregate. The pavement performance of colored asphalt mixture is enhanced, and the mechanism is studied. Silanols formed by the hydrolysis of silane coupling agent, and then reacted with the hydroxyl groups on the aggregate surface, which can effectively improve the interfacial force between colored asphalt cement and aggregate. Marshall test, immersion Marshall test, rutting test, and bending test under low temperature are conducted. The results indicate that the modified colored asphalt mixture by silane coupling agent exhibit fine performance at high and low temperature and moisture resistance.

关 键 词：彩色沥青 硅烷偶联剂 水稳性 高温稳定性 

分 类 号：U416.217[交通运输工程—道路与铁道工程]