Degradation behaviors of La–Mg–Ni-based metal hydride alloys:structural stability and influence on hydrogen storage performances  

作　　者：Yi-Ming Li Bao-Yu Duan Zhuo-Cheng Liu Yang-Huan Zhang Hui-Ping Ren 

机构地区：[1]Key Laboratory of Integrated Exploitation of Bayan Obo Multi-Metal Resources,Inner Mongolia University of Science and Technology [2]Analytical and Testing Center,Inner Mongolia University of Science and Technology

出　　处：《Acta Metallurgica Sinica(English Letters)》2018年第9期897-909,共13页金属学报（英文版）

基　　金：supported financially by the National Natural Science Foundation of China (No.51761032);the University Foundation of Inner Mongolia (No.NJZZ18142)

摘　　要：The present work focuses on the structural stability upon hydrogenation of three typical La-Mg-Ni-based alloys： La2 MgNi9, LaaMgNi14 and La4MgNi19. Structural changes during gaseous and electrochemical cycles were characterized, and the influence of the structure distortion on the hydrogen storage properties was concerned. Hydrogen-induced amor- phization （HIA） and disproportionation of the three alloys have occurred during both the gaseous and electrochemical cycles. Structural stability of the phase structures in the La-Mg-Ni system is found to follow the order： LaNi5- 〉 （La,Mg）5Ni19 〉 （La,Mg）2Ni7 〉 （La,Mg）Ni3 〉 （La,Mg）Ni2. HIA increases thermal stability of the metal hydrides and difficulty to dehydrogenation and leads to degradation of both the gaseous and electrochemical capacities. Interestingly, LaEMgNi9 with poor stability presents elevated discharge capability even at 60 ℃ which can be attributed to increase in the hydrogen desorption capability and inhibition of the self-discharge induced by severe HIA at higher temperatures. In addition, HIA in the electrochemical reactions is obviously weaker than the extent during the gaseous cycles, which is mainly due to the slower hydrogenation speed. The development of HIA in the gaseous and electrochemical process is considered to follow the direct and gradual modes, respectively.The present work focuses on the structural stability upon hydrogenation of three typical La-Mg-Ni-based alloys： La2 MgNi9, LaaMgNi14 and La4MgNi19. Structural changes during gaseous and electrochemical cycles were characterized, and the influence of the structure distortion on the hydrogen storage properties was concerned. Hydrogen-induced amor- phization （HIA） and disproportionation of the three alloys have occurred during both the gaseous and electrochemical cycles. Structural stability of the phase structures in the La-Mg-Ni system is found to follow the order： LaNi5- 〉 （La,Mg）5Ni19 〉 （La,Mg）2Ni7 〉 （La,Mg）Ni3 〉 （La,Mg）Ni2. HIA increases thermal stability of the metal hydrides and difficulty to dehydrogenation and leads to degradation of both the gaseous and electrochemical capacities. Interestingly, LaEMgNi9 with poor stability presents elevated discharge capability even at 60 ℃ which can be attributed to increase in the hydrogen desorption capability and inhibition of the self-discharge induced by severe HIA at higher temperatures. In addition, HIA in the electrochemical reactions is obviously weaker than the extent during the gaseous cycles, which is mainly due to the slower hydrogenation speed. The development of HIA in the gaseous and electrochemical process is considered to follow the direct and gradual modes, respectively.

关 键 词：La-Mg-Ni-based alloys Degradation behaviors Hydrogen-induced amorphization ELECTROCHEMICALPROPERTIES 

分 类 号：TG139.7[一般工业技术—材料科学与工程]