Influence of Nb Content on Microstructure and Mechanical Properties of a 7%Ni Steel  

作　　者：Hong-Wei Cao Xing-Hong Luo Guo-Feng Zhan Shi Liu 

机构地区：[1]School of Materials Science and Engineering,University ofScience and Technology of China,Shenyang 110016,China [2]CAS Key Laboratory of Nuclear Materials and SafetyAssessment,Institute of Metal Research,Chinese Academyof Sciences,Shenyang 110016,China [3]Research and Development Center of Wuhan Iron and Steel(Group)Corp,Wuhan 430080,China

出　　处：《Acta Metallurgica Sinica(English Letters)》2018年第9期975-982,共8页金属学报（英文版）

基　　金：financially supported by Wuhan Iron&Steel Co.,Ltd.

摘　　要：The influence of Nb content on the microstructure and cryogenic mechanical properties of a 7%Ni steel was investigated within the Nb content range from 0 to 0.05%. The microstructure was characterized by optical microscope, scanning electron microscope, transmission electron microscopy and X-ray diffraction, and the low-temperature mechanical property tests were conducted. The Nb addition can effectively refine the prior austenite grains and microstructure of the steel. Fine niobium precipitates with a diameter of about 10-50 nm were observed. They tend to be spherical and locate mainly in the vicinity of grain boundaries. Although there are considerable amounts of reversed austenite forming at grain boundaries in the specimen containing the highest Nb content, no Nb element was detected in such reversed austenite, which implies that Nb element did not affect the formation of the reversed austenite directly. Mechanical test results suggest that the strength of the 7%Ni steel is not simply in relation to the prior austenite grain size, but also depends on the amount of reversed austenite. On the other hand, the grain refinement, enhanced with increasing Nb content, has a good effect on cryogenic toughness.The influence of Nb content on the microstructure and cryogenic mechanical properties of a 7%Ni steel was investigated within the Nb content range from 0 to 0.05%. The microstructure was characterized by optical microscope, scanning electron microscope, transmission electron microscopy and X-ray diffraction, and the low-temperature mechanical property tests were conducted. The Nb addition can effectively refine the prior austenite grains and microstructure of the steel. Fine niobium precipitates with a diameter of about 10-50 nm were observed. They tend to be spherical and locate mainly in the vicinity of grain boundaries. Although there are considerable amounts of reversed austenite forming at grain boundaries in the specimen containing the highest Nb content, no Nb element was detected in such reversed austenite, which implies that Nb element did not affect the formation of the reversed austenite directly. Mechanical test results suggest that the strength of the 7%Ni steel is not simply in relation to the prior austenite grain size, but also depends on the amount of reversed austenite. On the other hand, the grain refinement, enhanced with increasing Nb content, has a good effect on cryogenic toughness.

关 键 词：7%Ni steel Nb content Niobium precipitate Reversed austenite Cryogenic mechanical properties 

分 类 号：TG142.1[一般工业技术—材料科学与工程]